牌号简介 About |
---|
Vibrathane 8590是一种聚酯基、MDI端接的液态聚氨酯预聚物,展示了Chemtura在聚氨酯工业这一重要领域的先进技术。这种新的预聚物具有很强的耐热老化性和对催化剂添加的均匀、可预测的反应性。当与1,4丁二醇固化时,这一成员的振动烷家族生产高质量的硫化,这是91肖氏A硬度。这些坚韧、高品质的弹性体的特点是:高撕裂强度、优异的耐磨性、良好的耐溶剂性、优异的弹性寿命Vibrathane® 8590,在加工温度下,粘度低,工作寿命适用于机器和手工配料程序。 VIBRATHANE 8590 is a polyester-based, MDI terminated liquid urethane prepolymer that exhibits Chemtura's advanced technology in this vital area of the polyurethane industry. This new prepolymer is highly unique in its resistance to heat aging and its uniform, predictable response to the addition of catalyst. When cured with 1,4 Butanediol, this member of the Vibrathane family produces high quality vulcanizates that is 91 Shore A hardness. These tough, high quality elastomers are characterized by: High Tear Strength Excellent Abrasion Resistance Good Solvent Resistance Excellent flex life Vibrathane 8590, at processing temperature, is low in viscosity and has a working life suitable for both machine and hand-batching procedures. |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
8.07 | MPa | ASTM D412 |
300% 应变 300% strain |
19.7 | MPa | ASTM D412 |
拉伸强度 tensile strength |
50.3 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
490 | % | ASTM D412 |
撕裂强度 tear strength |
|||
-- -- 2 |
107 | kN/m | ASTM D624 |
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability |
min | ||
后固化时间 Post curing time |
|||
115℃ 115℃ |
hr | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
115℃ 115℃ |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
压缩强度 compressive strength |
ASTM D695 | ||
5% 应变 5% strain |
MPa | ASTM D695 | |
10% 应变 10% strain |
MPa | ASTM D695 | |
15% 应变 15% strain |
MPa | ASTM D695 | |
20% 应变 20% strain |
MPa | ASTM D695 | |
25% 应变 25% strain |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
一次性处置兼容和分散两大难题
2018-07-19 一次性解决相容和分散两大难题“石墨烯应用目前遭遇瓶颈,我们的任务就是打破瓶颈。”在7月12日于江苏徐州举行的橡胶高峰论坛上,青岛科技大学教授辛振祥介绍,为突破石墨烯的应用瓶颈,他们以植物系材料作为分散助剂实现了石墨烯绿色宏量制备。同时,植物系材料的加入还一次性解决了石墨烯相容和分散性差两大难题,有助于打破石墨烯的应用瓶颈。 辛振祥介绍,该制备方法以石墨为原料,天然化合物―植物系材料作为分散助剂,水或有机溶剂为分散介质,采用超声或搅拌剪切的方法从石墨中剥离制备功能化石墨烯。< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |