Aegis® H100MP是一种润滑和有核的中等粘度尼龙6挤出级均聚物,用于浇铸或吹塑薄膜。符合21 CFR 177.1500的FDA要求以及欧盟指令2002/72/EC。它具有与尼龙6相关的强度、韧性和热成型性能,以及优异的耐热性、化学性和耐磨性。 Aegis® H100MP is a lubricated and nucleated medium viscosity nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to FDA requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermoforming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
235℃,1.0kg 235℃,1.0kg |
2.6 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
ASTM D570 | ||
24hr 24hr |
1.6 | % | ASTM D570 |
饱和 saturated |
9.5 | % | ASTM D570 |
平衡 balance |
2.7 | % | ASTM D570 |
含水量 water content |
% | ASTM D6869 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弹性模量 Elastic modulus 2 |
|||
TD TD 2 |
MPa | ASTM D882 | |
MD MD 2 |
MPa | ASTM D882 | |
拉伸强度 tensile strength 2 |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 2 |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
二氧化碳传输速率 Carbon dioxide transfer rate |
|||
23℃ 23℃ |
cm³/m²/24 hr | ASTM D1434 | |
氮传输速率 Nitrogen transfer rate |
|||
23℃ 23℃ |
cm³/m²/24 hr | ASTM D1434 | |
氧气传输速率 Oxygen transfer rate |
|||
23℃ 23℃ |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
23℃ 23℃ |
g/m²/24 hr | ASTM F1249 | |
Graves Tear Graves Tear |
ASTM D1004 | ||
MD:23℃ MD:23℃ |
N | ASTM D1004 | |
TD:23℃ TD:23℃ |
N | ASTM D1004 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Puncture Index(23℃) Puncture Index(23℃) 3 |
kN/m | ||
抗穿刺性 Puncture resistance 3 |
|||
23℃ 23℃ 3 |
g |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
3 ASTM D1306 |
【新闻资讯】查看全部
巴斯夫将扩展欧洲工程塑料产能
2015-12-01 预计从2017年开始,巴斯夫位于德国施瓦茨海德的工厂每年将增加7万吨聚酰胺(PA)Ultramid和聚对苯二甲酸乙二醇酯(PBT)Ultradur。这是巴斯夫针对全球工程塑料需求增加而采取产能扩展的一步。届时,巴斯夫全球PA、PBT的产能将超过每年70万吨。 巴斯夫将扩大欧洲工程塑料产能 今年年中,巴斯夫的上海工厂也将两种材料的产能提高了一倍,同时还提高热塑性聚氨酯(TPU)的产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |