牌号简介 About |
---|
Lexan Exl Filament AMHI240F是一款高冲击力的黑色聚碳酸酯产品。与标准聚碳酸酯相比,它在室温和极低温度下具有较高的冲击强度,并改善了UL94的性能。标称灯丝直径为1.79 mm±0.05 mm,线轴尺寸为1510 cc。 LEXAN™ EXL AMHI240F filament is a high impact polycarbonate product available in a black color. It provides high impact strength at room temperature and extreme low temperatures, in combination with improved UL94 performance over standard polycarbonate. Nominal filament diameter is 1.79 mm ± 0.05 mm and it is available in a 1510 cc spool size. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
XY 方向 XY direction |
1700 | MPa | |
XZ 方向 XZ direction |
1900 | MPa | |
ZX 方向 ZX direction |
1790 | MPa | |
拉伸强度 tensile strength 2 |
|||
XY 方向,断裂 XY direction, fracture |
45.0 | MPa | |
XZ 方向,断裂 XZ direction, fracture |
55.0 | MPa | |
ZX 方向,断裂 ZX direction, fracture |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
XY 方向,断裂 XY direction, fracture |
% | ||
XZ 方向,断裂 XZ direction, fracture |
% | ||
ZX 方向,断裂 ZX direction, fracture |
% | ||
弯曲模量 Bending modulus 3 |
|||
XY 方向 XY direction |
MPa | ||
XZ 方向 XZ direction |
MPa | ||
ZX 方向 ZX direction |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
XY 方向,-30℃ XY direction, -30 ℃ |
J/m | ||
XY 方向,23℃ XY direction, 23 ℃ |
J/m | ||
XZ 方向,-30℃ XZ direction, -30 ℃ |
J/m | ||
XZ 方向,23℃ XZ direction, 23 ℃ |
J/m | ||
ZX 方向,-30℃ ZX direction, -30 ℃ |
J/m | ||
ZX 方向,23℃ ZX direction, 23 ℃ |
J/m | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
ZX 方向:-30℃ ZX direction: -30 ℃ |
J/m | ||
XZ 方向:-30℃ XZ direction: -30 ℃ |
J/m | ||
XY 方向:-30℃ XY direction: -30 ℃ |
J/m | ||
ZX 方向:23℃ ZX direction: 23 ℃ |
J/m | ||
XZ 方向:23℃ XZ direction: 23 ℃ |
J/m | ||
XY 方向:23℃ XY direction: 23 ℃ |
J/m | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
-30℃,Total Energy -30℃,Total Energy 4 |
J | ||
-30℃,Total Energy -30℃,Total Energy 5 |
J | ||
23℃,Total Energy 23℃,Total Energy 5 |
J | ||
23℃,Total Energy 23℃,Total Energy 4 |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
XY 方向:1.8 MPa,未退火,3.20 mm XY direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
XZ 方向:1.8 MPa,未退火,3.20 mm XZ direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
ZX 方向:1.8 MPa,未退火,3.20 mm ZX direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
维卡软化温度 Vicat Softening Temp |
|||
-- -- 5 |
℃ | ASTM D1525 6 | |
-- -- 7 |
℃ | ASTM D1525 6 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:XY 方向 MD: XY direction |
1/℃ | ||
MD:ZX 方向 MD: ZX direction |
1/℃ | ||
MD:XZ 方向 MD: XZ direction |
1/℃ | ||
TD:XY 方向 TD: XY direction |
1/℃ | ||
TD:ZX 方向 TD: ZX direction |
1/℃ | ||
TD:XZ 方向 TD: XZ direction |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
XY 方向 XY direction |
ohms·cm | ||
ZX 方向 ZX direction |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
XY 方向:1.90 GHz XY direction: 1.90 GHz |
|||
ZX 方向:1.90 GHz ZX direction: 1.90 GHz |
|||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 8 |
|||
ZX 方向,3.00 mm ZX direction, 3.00 mm |
|||
XZ 方向,3.00 mm XZ direction, 3.00 mm |
|||
XY 方向,3.00 mm XY direction, 3.00 mm |
备注 |
---|
2. 类型 1, 5.0 mm/min |
3. 1.3 mm/min |
4. ZX Orientation |
5. XY Orientation |
6. 速率 A (50°C/h), 压 力1 (10N) |
7. XZ Orientation |
8. UL results provided herein may not be sufficient to waive end use part testing for UL listing. Contact UL for further details. |
【新闻资讯】查看全部
注塑模具设计时,应该留意这几种参数!
2019-03-11 注塑机上面有两个模板,一块不动,称为定模板;另外一块可以移动,称为动模板。模具就分别通过螺钉和压板固定在这两块模板上。开模时,注塑机的动模板移动,从而带动把模具打开 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |