牌号简介 About |
---|
Elastollan® 1185AW是一种基于聚醚的热塑性聚氨酯(TPU),含有增塑剂。它是专门为电线和电缆、薄膜和片材以及挤压成型应用而设计的。它含有非卤化阻燃剂,在0.75、1.5和3.0 mm壁厚的垂直火焰试验中,其额定值为UL-94V-2。它还通过了FAR 25.853(a)火焰测试。它具有优异的耐磨性、韧性、透明度、低温柔韧性、水解稳定性和抗真菌性。它具有优良的阻尼特性和优异的抗撕裂扩展性能。Elastcollan1185a以未着色的颗粒形式提供。 Elastollan® 1185AW is a polyether-based thermoplastic polyurethane (TPU) containing a plasticizer. It is specifically formulated for wire and cable, film and sheet, and extruded profile applications. It contains a non-halogenated flame retardant and is rated UL-94 V-2 in vertical flame test for wall thicknesses of 0.75, 1.5 and 3.0 mm. It also passes FAR 25.853 (A) flame test. It exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1185A is supplied uncolored in pellet form. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.16 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,3.80kg 190℃,3.80kg |
5.0 to 25 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
85 | ASTM D2240 | |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
19.3 | MPa | ASTM D412 |
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
20.7 | MPa | ASTM D790 |
泰伯耐磨性 Taber abraser |
mg | ASTM D1044 | |
Abrasion(DIN) Abrasion(DIN) |
mm³ | DIN 53516 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | 内部方法 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
软化温度 Softening temperature |
|||
DMA DMA |
℃ | Internal Method | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
甘肃甘浚落实废旧地膜回收率80%以上制度
2017-11-10 为建立健全废旧农膜回收体系,规范回收行为,提高农膜使用效率,切实保护农业生态环境。甘州区甘浚镇成立以镇长为组长,分管领导为副组长,其他领导及包村站所负责人为成员的工作领导小组,狠抓此项工作的落实。通过广泛宣传政策,提高群众认识,综合运用“红黑榜”、微信工作交流群等平台,激发群众参与的激情。同时,坚决落实废旧农膜回收保证金制度,采取盯紧看牢、上交废旧农膜清理保证金等措施,促使群众积极参与整治。 据悉,该镇严格执行废旧地膜回收率达到80%以上的制度。对未完成废旧农膜清理回收指标 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |