牌号简介 About |
---|
HEPLA®H2018cm EC是一种18%矿物填充材料。这种材料结合了高硬度和优良的耐温性和导电性,用于静电喷涂。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792 |
密度 Density |
1.25 | g/cm³ | ISO 1183 |
Moisture Absorption Moisture Absorption |
|||
平衡,23℃, 50% RH Equilibrium, 23 ℃, 50% RH |
1.1 | % | ISO 62 |
收缩率 Shrinkage rate |
|||
MD:3.20 mm MD:3.20 mm |
1.1 | % | NFD Method |
熔体质量流动速率 Melt Flow Rate |
|||
280℃,5.0 kg 280℃,5.0 kg |
16 | g/10 min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
220℃,5.0 kg 220℃,5.0 kg |
cm3/10min | ISO 1133 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1 | |
拉伸模量 Tensile modulus |
|||
5.0 mm/min 5.0 mm/min |
MPa | ASTM D638 | |
Tensile Stress, yield, Type I Tensile Stress, yield, Type I |
|||
5.0 mm/min 5.0 mm/min |
MPa | ASTM D638 | |
Tensile Stress, break, Type I Tensile Stress, break, Type I |
|||
5.0 mm/min 5.0 mm/min |
MPa | ASTM D638 | |
Tensile Strain, yield, Type I Tensile Strain, yield, Type I |
|||
5.0 mm/min 5.0 mm/min |
% | ASTM D638 | |
Tensile Strain, break, Type I Tensile Strain, break, Type I |
|||
5.0 mm/min 5.0 mm/min |
% | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/5 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
2.0 mm/min 2.0 mm/min |
MPa | ISO 178 | |
弯曲模量 Bending modulus |
|||
50.0 mm Span, 1.3 mm/min 50.0 mm Span, 1.3 mm/min |
MPa | ASTM D790 | |
Flexural Stress, yield Flexural Stress, yield |
|||
2.0 mm/min 2.0 mm/min |
MPa | ISO 178 | |
Flexural Stress, break Flexural Stress, break |
|||
50.0 mm Span, 1.3 mm/min 50.0 mm Span, 1.3 mm/min |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度, 23℃ Impact strength of cantilever beam notch, 23 ℃ |
J/m | ASTM D256 | |
Notched Izod Impact, -30℃ Notched Izod Impact, -30℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
80*10*4, 23℃ 80*10*4, 23℃ |
kJ/m2 | ISO 180/1A | |
80*10*4, -30℃ 80*10*4, -30℃ |
kJ/m2 | ISO 180/1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
80*10*4, -30℃ 80*10*4, -30℃ |
kJ/m2 | ISO 180/1U | |
80*10*4, 23℃ 80*10*4, 23℃ |
kJ/m2 | ISO 180/1U | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
80*10*4, 23℃ 80*10*4, 23℃ |
kJ/m2 | ISO 179/1eA | |
飞镖冲击强度 Dart impact strength |
|||
23℃, Total Energy 23℃, Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,64.0 mm Span, 120*10*4 mm 0.45 MPa, unannealed, 64.0 mm Span, 120 * 10 * 4 mm |
℃ | ISO 75-2/Be | |
0.45MPa,未退火,3.2mm 0.45MPa, unannealed, 3.2mm |
℃ | ISO 75-2/Be | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B50 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
Flow : 23 to 60℃ Flow : 23 to 60℃ |
1/℃ | ISO 11359-2 | |
Transverse : 23 to 60℃ Transverse : 23 to 60℃ |
1/℃ | ISO 11359-2 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
新疆美克化工新建2×30万吨/年BDO项目案审批通过
2022-05-08 近日,新疆美克化工股份有限公司230万吨/年BDO项目备案审批通过,项目采用天然气路线炔醛法工艺制备BDO。 此前3月31日,中泰集团董事长王洪欣在北京会见了中国石化集团审计部总经 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |