牌号简介 About |
---|
Moplen HP420M是一种高流动聚丙烯均聚物,设计用于在管状双气泡线和铸膜上生产双向拉伸聚丙烯薄膜(BOPP)。典型应用包括BOPP包装、层压膜和吸管,也包括食品包装,如面食、零食、饼干、面包制品和糖果、花卉包装膜、书籍、文具、毛毯、衬衫、针织品和丝袜。有关监管信息,请参阅Moplen HP420M产品管理公告(PSB)。 Moplen HP420M is a high flow polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP) on tubular double bubble lines and cast film. Typical applications are BOPP packaging, laminating film and drinking straws but also packaging foodstuffs such as pasta, snacks, biscuits, bakery products and confectionery, film for packaging for flowers, books stationery, blankets, shirts, knitwear and hosiery. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
8.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服 yield |
33.0 | MPa | ISO 527-2 |
断裂 fracture |
21.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
ISO 527-2 | ||
屈服 yield |
12 | % | ISO 527-2 |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
摩擦系数 friction coefficient |
|||
动态,铸造薄膜 Dynamic, cast thin film |
ASTM D1894 | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弹性模量 Elastic modulus 2 |
|||
TD,50 µm,铸造薄膜 TD, 50 µ m, cast thin film 2 |
MPa | 内部方法 | |
MD,50 µm,铸造薄膜 MD, 50 µ m, cast thin film 2 |
MPa | 内部方法 | |
拉伸强度 tensile strength 3 |
ASTM D882 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,断裂,50 µm,挤塑薄膜 MD, fracture, 50 µ m, extruded film |
% | ASTM D882 | |
TD,断裂,50 µm,挤塑薄膜 TD, fracture, 50 µ m, extruded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 4 |
g | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss 5 |
|||
45°,铸造薄膜 45 °, cast thin film 5 |
内部方法 | ||
雾度 Haze 6 |
|||
50 µm,铸造薄膜 50 µ m, cast thin film 6 |
% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 MA 18068 |
3 20 in/min |
4 MA17106 |
5 MA 17021 |
6 MA 17031 |
【新闻资讯】查看全部
航空业开展推进聚合物复合材料市值持续上扬
2016-06-27 根据透明度市场调研报告,2013年,全球高级聚合物复合材料市值为74.7亿美元,到2020年,预计增长到121.2亿美元,2014至2020年间的年复合增长率预计为7.2%。 航空业需求持续增长,是推动高级聚合物复合材料市场不断发展的主要因素。此外,聚合物复合材料在风能领域应用的不断增长,也是重要的推动因素。一方面,下游应用的不断扩大,为高级聚合物复合材料持续增长提供了重要机遇。另一方面,生产成本的快速增加,则又是抑制市场发展的主要因素。 复合材料由拥有不同 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |