牌号简介 About |
---|
SQ185 G6 FR3.0 GP 是30%玻璃纤维增强的PC材料,添加了内部脱模剂。特别适用于需要高硬度和高耐热性的应用。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比重 Specific Gravity Specific Gravity |
1.43 | ASTM D792 | |
特定体积 Specific volume Specific volume |
0.69 | cm³/g | ASTM D792 |
密度 Density Density |
1.44 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
ASTM D1238 | ||
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ASTM D1238 |
300℃,5.0kg 300℃,5.0kg |
19 | g/10min | ASTM D1238 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
流动,3.2 mm Flow, 3.2 mm |
% | 内部方法 | |
吸水率 Water Absorption Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ASTM D570 | |
24hr 24hr |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
落锤冲击 Gardner Impact Gardner Impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
拉伸冲击强度 Tensile Impact Strength Tensile Impact Strength |
kJ/m² | ASTM D1822 | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 5 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
比热 Specific Heat Specific Heat |
J/kg/℃ | ASTM C351 | |
导热系数 Thermal Conductivity Thermal conductivity |
W/m/K | ASTM C177 | |
相对温度指数 Relative Temp Index(RTI) Relative Temperature Index (RTI) |
|||
电气性能 Elec Electrical performance Elec |
℃ | UL 746 | |
强度机械性能 Str Strength mechanical performance Str |
℃ | UL 746 | |
冲击机械性能 Imp Impact mechanical performance Imp |
℃ | UL 746 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohm·cm | ASTM D257 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant Dielectric Constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation Factor Dissipation Factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc Resistance Arc Resistance |
ASTM D495 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High Voltage Arc Track Rate High Voltage Arc Track Rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot Wire Ignition Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.47 mm 1.47 mm |
UL 94 | ||
2.99 mm 2.99 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂 brk Broken BRK |
MPa | ASTM D638 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk Broken BRK |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
50 mm 50 mm |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
屈服 yld,50 mm Yield yld, 50 mm |
MPa | ASTM D790 | |
泰伯耐磨性 Taber Abrasion Taber Abrasion |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
洛氏硬度 Rockwell Hardness Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
“抢购”!销售合同27.44亿元的聚氨酯新材料受到中国大船厂青睐
2023-01-12 扫描上图二维码,可以免费下载 搜料 APP 近日,江苏雅克科技陆续发布公告。该公司及下属孙公司斯洋国际有限公司分别与沪东中华造船、中国船舶工业贸易、江南造船等企业签订了液 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |