产品描述:trexprene A55ni是一种热紫外线稳定的PP/EPDM基热塑性硫化弹性体(TPV)。这种天然化合物主要用于室内应用,可以使用注塑、挤压、吹塑或其他熔融加工技术进行加工。 Product Description: TREXPRENE ® A55NI is a heat and UV stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This Natural compound is primarily intended for interior applications can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 to 0.980 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ISO 37 | ||
TD,100% 应变 TD, 100% strain |
1.80 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
3.40 | MPa | ISO 37 |
拉伸强度 tensile strength 2 |
ISO 37 | ||
断裂 fracture |
4.80 | MPa | ISO 37 |
MD,断裂 MD, fracture |
3.70 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
ISO 37 | ||
断裂 fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength 3 |
ISO 34-1 | ||
TD TD |
kN/m | ISO 34-1 | |
MD MD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 4 |
|||
70℃,24 hr 70℃,24 hr |
% | ASTM D395B | |
70℃,24 hr 70℃,24 hr 4 |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒 Shore A, 15 seconds |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
Brittleness Temperature(Type B) Brittleness Temperature(Type B) |
℃ | ISO 812 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 在空气中(110℃,1000 hr) The rate of change in tensile strength in air (110 ℃, 1000 hr) |
% | ISO 188 | |
Change in Tensile Strain at Break in Air(110℃,1000 hr) Change in Tensile Strain at Break in Air(110℃,1000 hr) |
% | ISO 188 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Fogging(Dry Fog) Fogging(Dry Fog) |
% | SAE J1756 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加速老化时间 Accelerated aging time 5 |
|||
颜色稳定性 Color stability |
|||
to Burnt Gas,AATCC Rating:60℃ to Burnt Gas,AATCC Rating:60℃ 6 |
|||
to Burnt Gas,Change in Color:60℃ to Burnt Gas,Change in Color:60℃ 6 |
|||
to Burnt Gas,黄度指数:60℃ To Burnt Gas, Yellowness Index: 60 ℃ 6 |
YI | ||
to Light to Light 7 |
|||
Odor Rating Odor Rating 8 |
|||
耐臭氧性 Ozone resistance 9 |
|||
40℃ 40℃ 9 |
ISO 1431-1 | ||
耐候性 Weathering resistance |
|||
Arizona Arizona 10 |
|||
Florida Florida 11 |
SAE J1976 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 20 in/min |
3 B 方法,直角形试样(不割口), 20 in/min |
4 类型 A |
5 Filtered Xenon per FLTM BO 116-01, 2481.6 kJ/m² |
6 ISO 105-G02, AATCC TM 23, 168 h |
7 SAE J2412, ISO 105-B06, Cond. 5, 1,240.8 kJ/m² |
8 100 pphm, Method A |
9 105,000 TNR Langleys exposure per GMW3417 L1, F2, G1, T5 |
10 2 years exposure, Procedure A |
11 GMW3205 Code B |
【新闻资讯】查看全部
帝人汽车专访:先进复合材料如何助力未来出行?
2022-01-05 搜料网资讯: 快速发展的电动汽车,带动了产业链对锂电池、结构件的相关需求。汽车制造商和原始设备制造商在开发新电动汽车时,面临最大的挑战是车辆续航里程、电池安全性和电 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |