牌号简介 About |
---|
XDS34是一种低密度聚乙烯,专为各种大尺寸(70-200微米)薄膜应用而设计。XDS34不含任何添加剂。XDS34适用于包装袋、托盘包装和各种需要大尺寸(70-200微米)薄膜的工业薄膜。 Alkathene XDS34 is a low density polyethylene designed for a variety of heavy gauge (70 - 200µm) film applications. Alkathene XDS34 does not contain any additives. Film Extrusion: Alkathene XDS34 is intended for applications such as sacks, palletwrap, shrink film and a variety of industrial films requiring heavy gauge film. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.30 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
100 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:100 µm,吹塑薄膜 2% secant, MD: 100 µ m, blow molded film |
130 | MPa | ASTM D882 |
2% 正割,TD:100 µm,吹塑薄膜 2% secant, TD: 100 µ m, blow molded film |
140 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,100 µm,吹塑薄膜 MD, yield, 100 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,100 µm,吹塑薄膜 TD, yield, 100 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,100 µm,吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,100 µm,吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,100 µm,吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,100 µm,吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
100 µm,吹塑薄膜 100 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:100 µm,吹塑薄膜 MD: 100 µ m, blow molded film |
g | ASTM D1922 | |
TD:100 µm,吹塑薄膜 TD: 100 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,100 µm,吹塑薄膜 45 °, 100 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
100 µm,吹塑薄膜 100 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
【干货】PP板的产品性能
2021-03-16 搜料网资讯: 玻纤增强PP板(FRPP板):通过20%被玻纤增强后,除保持原有的优良性能外,强度,刚性等均较PP提高一倍,而且具有良好的耐热性,低温冲击性,防腐耐电弧性,低收缩率。特 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |