牌号简介 About |
---|
西湖聚乙烯EF796是一种低密度配方,建议用于需要良好平衡性能的薄膜应用,如工业包装和通用包装用转化膜。 Westlake Polyethylene EF796 is a low density formulation suggested for film applications requiring a good balance of properties such as converter film for industrial packaging and general-purpose packaging. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.921 | g/cm³ | ASTM D4883 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,38 µm,吹塑薄膜 1% secant, TD, 38 µ m, blow molded film |
220 | MPa | ASTM D882 |
1% 正割,MD,38 µm,吹塑薄膜 1% secant, MD, 38 µ m, blow molded film |
186 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38 µm,吹塑薄膜 45 °, 38 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38.1 µm,吹塑薄膜 38.1 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
埃克森美孚新加坡光滑脂及分解光滑油厂扩建工程竣工
2017-06-06 ・ 埃克森美孚新加坡工厂是世界领先的合成机油品牌――美孚1号™在亚太区唯一的生产地 ・ 新增产能帮助满足亚太区市场对润滑脂和合成润滑油不断增长的需求 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |