牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种软质、黑色、特种非吸湿性热塑性硫化弹 性体(TPV)。它专门配制用于与 ABS、PS、PC、PMMA、ASA、PET 和 PPO/PS 共混 物粘结,适合于要求硬/软材料组合的应用。这一牌号的山都平 TPV 是剪切速率依 赖型产品,可在常规热塑性注塑成型或挤出成型设备上加工。这是一种聚烯烃基材 料,可在生产过程中进行回收利用。 A soft, black, specialty, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is especially formulated to bond to ABS, PS, PC, PMMA, ASA, PET and PPO/PS blends for applications where hard/soft combinations are required. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is polyolefin based and recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
600 | % | ISO 37 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
600 | % | ASTM D412 |
压缩形变 Compression deformation |
|||
125℃,70 hr 125℃,70 hr |
55 | % | ISO 815 |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 188 | ||
100℃,168 hr 100℃,168 hr |
% | ISO 188 | |
125℃,168 hr 125℃,168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 188 | ||
100℃,168 hr 100℃,168 hr |
% | ISO 188 | |
125℃,168 hr 125℃,168 hr |
% | ISO 188 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 A,100℃,168 hr Shaw A, 100 ℃, 168 hr |
ASTM D573 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 A,100℃,168 hr Shaw A, 100 ℃, 168 hr |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr |
ISO 188 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 1817 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 1817 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ISO 1817 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.10 mm 1.10 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1 |
3 类型 A |
【新闻资讯】查看全部
石化工程界“一带一路”寻机遇
2017-06-08 6月7日,以“‘一带一路’寻机遇、携手共进谋发展”为主题的首届北京国际工程发展论坛举行。会议认为,在石化行业“走出去”的大潮中,石化工程企业要成为行业抱团出海的核心,走在行业集群“走出去”的前列。 中国石油 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |