牌号简介 About |
---|
22302是一种LLDPE吹塑薄膜等级,设计用于即使在较低的挤出温度下也需要易于加工和良好光学性能的应用。该树脂非常适合与低密度聚乙烯(LDPE)混合,也适用于包括农业应用在内的一般用途。特点:通用易加工性好,光学性能好,挤出温度低,适合与低密度聚乙烯(LDPE)农业应用混合,吹塑薄膜级。 22302 is a LLDPE blown film grade designed for applications requiring ease of processing and good optical properties even at low extrusion temperature. This resin is well suited for blending with LDPE and for general pupose uses, including agricultural applications. Features General purpose Ease of processing Good optical properties Low extrusion temperature Suited for blending with LDPE Agricultural applications Applications Blown film grade |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.8 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
12.0 到 150 | µm | |
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
2% 正割,MD:25 µm,吹塑薄膜 2% secant, MD: 25 µ m, blow molded film |
175 | MPa | |
2% 正割,TD:25 µm,吹塑薄膜 2% secant, TD: 25 µ m, blow molded film |
MPa | ||
拉伸强度 tensile strength |
|||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ||
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ||
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
2016年上半年齐鲁石化小时乙烯产量过百吨
2016-07-21 2016年上半年,齐鲁石化烯烃厂平均小时乙烯产量实现100.5吨,累计乙烯产量较去年同期增加0.9万吨,增效明显。 “前些年乙烯市场不好,说起增产增效来,我们总是觉得有劲使不出来”,烯烃厂裂解车间主任房炳昌说到。2016年以来,化工市场好转,尤其是乙烯产品边际贡献较高,一吨产品过千元的效益,这让大家憋了许久的劲儿终于有了施展的地方,他们从装置的安稳生产入手,抓好关键设备运行,下力气啃下乙烯原料优化这块“硬骨头”,努力提高装置的负荷。今年以来,乙烯装置保持高负荷生产态势,其中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |