牌号简介 About |
---|
普立万的长纤维热塑性(LFT)化合物是为要求高硬度和良好冲击的应用而配制的,如金属替换或其他结构应用。与标准短纤维产品相比,这些产品具有更高的物理和机械性能。LFT化合物的好处包括改善冲击强度、弹性模量和材料强度,范围从亚环境到高度升高。此外,与传统的高填充短纤维产品相比,LFT化合物在蠕变和疲劳性能方面提供了改进的性能,提高了尺寸稳定性,并表现出优异的表面光洁度。 PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.59 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate 3 |
0.20 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
15500 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
208 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
1.8 | % | ISO 527-2 |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179 | |
落锤冲击 Drop hammer impact |
J | ASTM D5420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processing conditions. |
【新闻资讯】查看全部
美军用热塑性弹性体资料造通明轻质装甲
2017-03-15 美国海军研究实验室(NRL)的研究人员开发出一种透明的热塑性弹性体装甲,并申请了专利。与一般的防弹玻璃相比,新研制的装甲不仅具有极佳的防弹性能,且质量更轻。 热塑性弹性体是通过物理方法而非化学方法使柔软的橡胶聚合物固化而形成的,而固化过程是可逆的,因此能够就地修复受损的装甲的表面。研究人员称,在高于软化点的温度(100℃左右)加热受损装甲,融化小的晶体使断裂表面融合并通过扩散实现重组。这个过程的完成需要有一个诸如烙铁的热金属板作为模板,使新形成的表面成为一个光滑平整的薄板。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-OnForce™ LFT LF6600-5018 X2 NHFR NATURAL证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)