牌号简介 About |
---|
一种双组分高Tg透明环氧树脂,用于光纤电缆和组件的包装和组装。建议将光纤端接到金属箍中,或制作波导器件。它是EPO-TEK 353的快速固化替代品。符合美国药典第六类生物相容性标准。 A two component, high Tg, optically clear epoxy for packaging and assembly of fiber optics cables and components. It is suggested for termination of fibers into ferrules, or fabrication of waveguide devices. It is a faster curing alternative to EPO-TEK® 353ND. Complies with USP Class VI biocompatibility standards. |
技术参数 Technical Data | |||
---|---|---|---|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 5 |
1.570 | ||
透光率 Transmittance |
|||
700-1400 nm 700-1400 nm |
> 95.0 | % | |
1550 nm 1550 nm |
95.0 | % | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Degradation Temperature Degradation Temperature |
℃ | ||
Die Shear Strength(>10 kg,23℃) Die Shear Strength(>10 kg,23℃) |
MPa | ||
工作温度 working temperature |
|||
Continuous Continuous |
℃ | ||
Intermittent Intermittent |
℃ | ||
Storage Modulus(23℃) Storage Modulus(23℃) |
GPa | ||
加热减量 Heating reduction |
|||
200℃ 200℃ |
% | ||
250℃ 250℃ |
% | ||
300℃ 300℃ |
% | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 6 |
|||
-- -- 7 |
|||
密度 Density |
|||
Part B Part B |
g/cm³ | ||
Part A Part A |
g/cm³ | ||
粘度 viscosity 8 |
|||
23℃ 23℃ 8 |
Pa·s | ||
固化时间 Curing time |
|||
150℃ 150℃ |
hr | ||
储存稳定性 storage stability |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
搭接剪切强度 lap shear strength |
|||
23℃ 23℃ |
MPa | ||
相对电容率 Relative permittivity |
|||
1 kHz 1 kHz |
|||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature 2 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-- -- 3 |
3.6E-5 | cm/cm/℃ | |
-- -- 4 |
1.7E-4 | cm/cm/℃ | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
|||
23℃ 23℃ |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
3 Below Tg |
4 Above Tg |
5 589 nm |
6 Part B |
7 Part A |
8 100 rpm |
【新闻资讯】查看全部
中泰化学停止采购美克化工 拟投资51.16亿元自建30万吨BDO
2022-06-10 6月7日晚,中泰化工宣布,决定停止收购MEC化工75.89%的股份。美克化工拥有BDO产业链,中泰化工拥有集煤炭-热电-氯碱化工-粘胶纤维-粘胶纱上下游为一体的完整循环经济产业链。 今年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |