牌号简介 About |
---|
Infino TK-2046HD是一种聚对苯二甲酸环己基二亚甲酯 (PCT)产品,含有的填充物为玻璃纤维增强材料。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 Infino TK-2046HD is a Polycyclohexylenedimethylene Terephthalate (PCT) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Reflectors. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
- - |
1.53 | g/cm³ | ISO 1183 |
|
1.53 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,2.16kg 300℃,2.16kg |
60 | g/10min | ASTM D1238 |
300℃,2.16kg 300℃,2.16kg |
60 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
66.0 | MPa | ASTM D638 |
屈服 yield |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture |
% | ISO 527-2/5 | |
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 3 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 4 |
|||
23℃ 23℃ 4 |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 4 |
|||
23℃ 23℃ 4 |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ 4 |
kJ/m² | ISO 180-1A | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 4 |
|||
-5℃ -5℃ 4 |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
黄度指数 Yellowness index |
ASTM D1925 | ||
-- -- |
YI | ASTM D1925 | |
3.20 mm 3.20 mm |
YI | ASTM D1925 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 0.11 in/min |
4 Thickness: 4mm |
【新闻资讯】查看全部
细菌“小社会”能“吃掉”塑料
2016-11-15 喝完丢弃的矿泉水瓶、海洋里的塑料垃圾……这些随处可见的废弃塑料是大自然中难以被降解的顽固垃圾,威胁着地球的环境。传统塑料垃圾的处理方法需要高温集中处理,能耗高、效率低,还会造成二次污染。有没有更好的方法?有,可以让细菌把它们都“吃掉”。这就是天津大学化工学院本科生团队的研发成果:基于混菌体系的高效塑料生物降解系统。日前,该研究成果获得由美国麻省理工学院主办的2016国际遗传工程机器设计竞赛(iGEM)金奖及最佳环境项目单项奖提名。 混菌系统是一种人工设计的细菌组织方式,就像 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |