牌号简介 About |
---|
Daplen™ EF267AI是一种20%矿物填充聚丙烯化合物,用于注塑成型。这种材料在冲击强度和刚度之间具有极好的平衡,并且易于加工。 Daplen EF267AI is a 20% mineral filled polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness and is easy to process. Applications Dashboards Door panels and pockets Center consoles Other automotive interior parts Special Features Daplen EF267AI has been developed especially for the car industry to be used in automotive interior parts. Good scratch resistance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
16 | g/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
1.1 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃ -20℃ |
2.8 | kJ/m² | ISO 179/1eA |
23℃ 23℃ |
6.5 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-20℃ -20℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-20℃ -20℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion 4 |
|||
MD MD 4 |
1/℃ | 内部方法 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Fogging(16 h,100℃) Fogging(16 h,100℃) |
mg | DIN 75201 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
排放 discharge |
µgC/g | VDA 277 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 3 |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
3.50% 应变 3.50% strain |
MPa | ISO 178 | |
-- -- |
MPa | ISO 178 | |
弯曲应变 Bending strain |
% | ISO 178 | |
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 disk |
3 0.079 in/min |
4 -30°C/80°C |
【新闻资讯】查看全部 ![]()
增白剂除了作为塑料助剂 还被使用于哪些范畴?
2017-10-12 增白剂是一类能提高纤维织物和纸张等白度的有机化合物。又称光学增白剂、荧光增白剂。织物等常常由于含有色杂质而呈黄色,过去都采用化学漂白的方法进行脱色,采用在制品中添加增白剂的办法。 增白剂的作用是把制品吸收的不可见的紫外线辐射转变成紫蓝色的荧光辐射,与原有的黄光辐射互为补色成为白光,提高产品在日光下的白度。增白剂已经广泛应用在纺织、造纸、洗衣粉、肥皂、橡胶、塑料、颜料和油漆等方面。在塑料行业,是常用的塑料助剂 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |