牌号简介 About |
---|
Clearflex H&T CLH 196是一种含抗氧化剂的线性低密度聚乙烯(C6-LLDPE),适用于铸膜挤出。用Clearflex H&T CLH 196制造的拉伸薄膜具有优异的断裂力学性能,主要是沿机器方向的Elmendorf撕裂强度(MD)和抗穿刺性。此外,在自动包装机上使用时,保持力是这些薄膜的关键性能。推荐使用Clearflex H&T CLH 196生产超强力拉伸薄膜。它的性能,特别是在保持力和抗穿刺性方面,使Clearflex H&T CLH 196成为包装不规则形状货物和需要优越机械强度的应用的理想选择。 Clearflex H&T CLH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films manufactured with Clearflex H&T CLH 196 have outstanding fracture mechanical properties, mainly Elmendorf tear strength along machine direction (MD) and puncture resistance. Moreover, the holding force is the key property of these films when used in automatic wrapping machines Main Application Clearflex H&T CLH 196 is recommended for production of super-power stretch films. Its properties, especially in terms of holding force and puncture resistance, make Clearflex H&T CLH 196 the ideal choice for packaging goods of irregular shape and for applications requiring a superior mechanical strength. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.916 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.5 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,铸造薄膜 With oneself - dynamic, casting thin films |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
23 | µm | |
薄膜厚度 film thickness |
8 to 50µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,23 µm,铸造薄膜 1% secant, MD, 23 µ m, cast thin film |
MPa | ISO 527-3 | |
1% 正割,TD,23 µm,铸造薄膜 1% secant, TD, 23 µ m, cast thin film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,23 µm,吹塑薄膜 MD, yield, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,23 µm,吹塑薄膜 TD, yield, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,23 µm,吹塑薄膜 MD, fracture, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,23 µm,吹塑薄膜 TD, fracture, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,23 µm,铸造薄膜 MD, fracture, 23 µ m, cast thin film |
% | ISO 527-3 | |
TD,断裂,23 µm,铸造薄膜 TD, fracture, 23 µ m, cast thin film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
23 µm,铸造薄膜 23 µ m, cast thin film 2 |
g | ISO 7765-1/A | |
撕裂强度 tear strength 3 |
ISO 6383-2 | ||
MD,23 µm MD,23 µm |
kN/m | ISO 6383-2 | |
TD,23 µm TD,23 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,23 µm,铸造薄膜 45 °, 23 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
23 µm,铸造薄膜 23 µ m, cast thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Cast Film |
【新闻资讯】查看全部
原油暴跌,聚乙烯市场望风披靡
2021-11-29 搜料网资讯: 11月26日,南非发现特征明显不同于以往的新变异毒株,引发市场对于经济和需求前景的严重担忧,叠加此前美国将释放战略储备和美联储将加快收缩QE的预期,国际原油市 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |