牌号简介 About |
---|
抗环境应力开裂(ESCR)HIPS。IceR830D具有较高的抗冲击强度,对油、脂肪和化学试剂(如工业和家用清洁剂)具有更好的耐化学性。特别为冰箱行业开发,其中碳氢化合物或氟利昂用作聚氨酯绝缘泡沫的发泡剂。名称:热塑性塑料ISO 2897-PS-I、G、O88-O3-O7-12应用。该等级适用于挤压/热成型和注射成型。典型的应用是冰箱的内衬和框架,以及脂肪食品的包装容器。ICE R 830D显著改善了热成型过程中的壁厚分布,并允许优化原始挤压板的厚度。 Environmental stress cracking resistant (ESCR) HIPS. ICE R 830D combines high impact strength with an improved chemical resistance to oils, fats and chemical agents, such as detergents for both industrial and domestic use. Developed in particular for the fridge sector where hydrocarbons or freons are used as blowing agents for PU insulating foams. Designation: Thermoplastics ISO 2897-PS-I,G,O88-O3-O7-12 Applications This grade is suitable for extrusion/thermoforming and injection moulding. Typical applications are inner liners and frames for refrigerators and packaging containers for fatty foods. ICE R 830D significantly improves the wall thickness distribution in thermoforming and allows to optimize the thickness of the original extruded sheet. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.65 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
3.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.40 到 0.70 | % | 内部方法 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.10 | % | ISO 62 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ISO 180-4A | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
50 Hz 50 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.50 mm,所有颜色 1.50 mm, all colors |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-13 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ISO 2039-2 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
ISO 527-2/50 | ||
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
弯曲强度 bending strength 2 |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
聚氨酯夹芯板的优势市场剖析与开展方向
2016-04-21 氨酯夹芯板优势比较 1、EPS、XPS、PU的比较 在我们目前常接触到的隔热材料中,一般是EPS、XPS、PU这三种,我们就各自的特性和发展趋势作一分析。 EPS是可发性聚苯乙烯,是一种热塑性塑料,其优点是成本低廉,隔热性能较好,但阻燃性能极差,粘接性能一般,所以只能是过渡型产品。 XPS又叫挤塑聚苯乙烯泡沫板,其加工工艺是将聚苯乙烯的废料颗粒重新熔融,高温高压挤出的过程中注入氟里昂等发泡剂, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |