牌号简介 About |
---|
LF-Y819-A(基树脂):工业包装,收缩膜,与LLDPE的混合物,小直径管道和管道LF-Y819-C(防堵塞):工业包装,衬垫,收缩膜,与LLDPE的混合物 LF-Y819-A (Base resin): Industrial packaging, shrink film, blends with LLDPE, small diameter pipe and tubing LF-Y819-C (Antiblock): Industrial packaging, liners, shrink film, blends with LLDPE |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.75 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
薄膜厚度 film thickness |
> 25µm | ||
割线模量 Secant modulus |
|||
1% 正割,TD,38 µm,吹塑薄膜 1% secant, TD, 38 µ m, blow molded film |
225 | MPa | ASTM D882 |
1% 正割,MD,38 µm,吹塑薄膜 1% secant, MD, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
MD,38 µm,吹塑薄膜 MD, 38 µ m, blow molded film |
g | ASTM D1922 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38 µm,吹塑薄膜 45 °, 38 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
低摩擦穿刺 Low friction puncture |
|||
吹塑薄膜,38.0 µm Blow molded film, 38.0 µ m |
J/cm | Internal Method |
备注 |
---|
1 LF-Y819-A, LF-Y819-C and LF-Y819-D are subject to the specific limitation that they may not be used in articles used for packing or holding food during cooking. |
2 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
宝马将回收渔网制成的再生聚酰胺用于汽车地板和脚垫
2021-09-29 搜料网资讯: 可持续发展已经成为汽车行业的一个战略重点,汽车公司越来越多地使用可持续材料,其中62%的组织声称拥有全面的可持续发展战略。 自2016年以来,宝马集团使用基于回 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |