牌号简介 About |
---|
Noryl V01525是一种15%研磨纤维增强,注塑成型等级。该树脂具有良好的尺寸稳定性和低翘曲性,还使用了无氯化、无溴的FR添加剂,以达到1.60 mm时的V0 UL94额定值。对于要求低翘曲和薄壁FR性能的应用,Noryl V01525可能是一种很好的材料候选者。 NORYL V01525 is a 15% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 1.60 mm. NORYL V01525 is may be an excellent material candidate for application requiring low warpage and thin wall FR performance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.13 | g/cm³ | ASTM D792 |
-- -- |
1.25 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,5.0kg 300℃,5.0kg |
24 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
280℃,5 kg 280℃,5 kg |
10.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD 3 |
0.30 到 0.50 | % | |
MD:3.2 mm MD:3.2 mm |
% | ||
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 9 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ||
23℃ 23℃ |
J/m | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 10 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 11 |
℃ | ISO 75-2/Ae | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 12 | |
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
123~127℃ 123~127℃ |
|||
125℃ 125℃ 13 |
|||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ||
相对电容率 Relative permittivity |
|||
50 Hz 50 Hz |
|||
60 Hz 60 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
|||
60 Hz 60 Hz |
|||
1 MHz 1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.20 mm 1.20 mm |
|||
1.50 mm 1.50 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
-- -- 4 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 5 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 5 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 5 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 7 , 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 6 |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | 内部方法 |
备注 |
---|
3. Tensile Bar |
4. 5.0 mm/min |
5. 类型 1, 5.0 mm/min |
6. 1.3 mm/min |
7. 2.0 mm/min |
8. at Break |
9. 80*10*4 sp=62mm |
10. 80*10*4 mm |
11. 120*10*4 mm |
12. 速率 A (50°C/h), 载荷2 (50N) |
13. Approximate Maximum |
【新闻资讯】查看全部
恩格尔持续壮大――公司有史以来最大的投资项目
2018-04-23 恩格尔持续成长。这家总部位于奥地利 Schwertberg 的注塑机制造商和系统解决方案提供商已连续四年年营业额攀升。截至 2017/18 财年 3 月底,企业集团该财年营业额实现 15.1 亿欧元,比去年增加了11 %。 “2017/18 财年,光是上海工厂的设备销售量就比上一年增长了约 20%。”恩格尔企业集团首席战略官 Christoph Steger 于 2018 年 4 月底在上海举办的国际橡塑展开幕之际,就 17/18 财年情 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |