牌号简介 About |
---|
SABIC® PPcompound 7700是一种矿物填充改性聚丙烯。这种材料结合了高刚度,良好的冲击和高流动性和良好的油漆性。这种材料具有很宽的加工窗口和良好的物理性能。典型应用包括喷漆和非美学的汽车内部零件,如仪表板、上下仪表板、门板和装饰件。SABIC® PPcompound 7700是指定的汽车等级。 SABIC® PPcompound 7700 is a mineral filled modified polypropylene. This material combines high stiffness, good impact and high flow with good paintability. This material has a very broad processing window combined with good esthical performance. Typical applications include painted and non esthetic automotive interior parts such as instrument panels, lower and upper dashboard, door panels and trim. SABIC® PPcompound 7700 is a designated automotive grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
20 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
24 hrs 24 hrs |
0.75 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,注塑成型 23 ℃, injection molding |
无断裂 | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-40℃,注塑成型 -40 ℃, injection molding |
20 | kJ/m² | ISO 179/1eU |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/4A | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-4A | |
0℃,注塑成型 0 ℃, injection molding |
kJ/m² | ISO 180-4A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-4A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM D696 | ||
-30 到 30℃ -30 to 30 ℃ |
cm/cm/℃ | ASTM D696 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ASTM D696 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/5/50 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/5/50 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ISO 527-2/5/50 | |
拉伸应变 Tensile strain |
|||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ISO 527-2/5/50 | |
弯曲模量 Bending modulus 2 |
|||
注塑成型 injection molding 2 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 I (三点负荷) |
【新闻资讯】查看全部
公主岭市采取无效措施扎实推进“禁塑”任务
2017-09-04 今年以来,公主岭市扎实推进禁塑工作,出真招、鼓实劲、求实效,坚决遏制塑料污染行为,服务岭城环境安全。 一是明确任务,落实责任。各相关部门明确具体工作目标和责任,确定由公主岭市市场监管局各分局一名领导抓工作,组织分局执法人员对辖区内的商场、超市、集贸市场为重点区域,以塑料制品批发零售者、宾馆、餐厅、水果蔬菜店、食杂店、冷饮店、干洗店、药店等为重点对象的经营场所进行检查。 二是确定重点,狠抓源头。检查重点放在商场、超市、集贸市场和塑料袋批发业户,切断批发零售经营 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |