Techsil IS803是一种随时可用的单组分室温硫化(RTV)弹性体,在潮湿空气中固化,形成永久弹性橡胶。Techsil IS803在其固化状态下具有优异的耐温性。建议用于需要具有良好粘合性能的高模量密封剂的工业应用。主要特点是良好的电气绝缘。耐老化、耐风化、耐臭氧和耐电晕。抗氧化性和许多油、化学品和溶剂。与多种基板的良好结合。灵活性从-60°C到+300°C。 TECHSIL IS803 is a ready to use, one part room temperature vulcanising (RTV) elastomer, which cures on exposure to moist air to give a permanently elastic rubber. TECHSIL IS803 has excellent temperature resistance in its cured state. It is recommended for industrial applications where a high modulus sealant with good adhesive properties is required. Key Features Good Electrical Insulation. Resistance to ageing, weathering, ozone and corona. Resistance to oxidation and many oils, chemicals and solvents. Excellent bonding to a wide range of substrates. Flexibility from -60°C to +300°C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.07 | g/cm³ | BS 903 |
收缩率 Shrinkage rate |
|||
MD MD |
< 0.80 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
IRHD 硬度 IRHD hardness |
38 | BS 903 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
剥离强度 peel strength |
5.3 | kN/m | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 1 |
|||
屈服 yield 2 |
2.30 | MPa | BS 903 |
100% 应变 100% strain 1 |
MPa | BS 903 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
% | BS 903 | |
撕裂强度 tear strength 4 |
kN/m | BS 903 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time 7 |
|||
23℃,3.00 mm 23℃,3.00 mm 7 |
hr | ||
挤出速率 Extrusion rate |
g/min | ||
Young's Modulus Young's Modulus 8 |
MPa | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
TD TD |
1/℃ | ||
导热系数 Thermal conductivity coefficient |
W/m/K | ||
使用温度 Operating temperature 5 |
℃ | ||
Tack Free Time(23℃) Tack Free Time(23℃) 6 |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 AFS 1540B |
3 at 100% Strain |
【新闻资讯】查看全部
芜湖聚赛龙新资料科技无限公司正式揭牌
2018-06-07 6月2日,广州市聚赛龙工程塑料股份有限公司华东生产基地――芜湖聚赛龙新材料科技有限公司正式揭牌。 广州市聚赛龙工程塑料股份有限公司成立于1998年,是专业从事塑料改性、工程塑料合金、功能高分子材料及热塑性弹性体研发、生产、销售和技术支持服务的省高新技术企业。公司拥有雄厚的研发力量和技术创新能力,先后多次承担国家、省市科技项目,自主研发的产品。工厂具备年产8万吨改性塑料的生产能力,公司研发中心拥有各类先进的材料研发设备和检测仪器。产品被广泛应用于汽车、家电、电子电器、电动工具 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |