牌号简介 About |
---|
JPHIPSE是一种高冲击聚苯乙烯,与其他HIPS树脂相比,具有良好的流动性、韧性、刚度和耐热性平衡。它适用于刚度和韧性以及可修边性很重要的挤压应用。JPHIPSE也常用于深拉热成型和注射成型。该产品的主要用途是在电器和家庭用品,以及食品包装和一次性应用,如杯子,盖子和服务用具。 JPHIPSE is a high impact polystyrene with an excellent balance of flow, toughness, stiffness and heat resistance as compared to other HIPS resins. It is appropriate for extrusion applications where stiffness and toughness combined with trimmability are important. JPHIPSE is also commonly used for deep draw thermoforming and injection molding. A major use of this product is in appliances and housewares as well as food packaging and disposables applications such as cups, lids and serviceware. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
2.8 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.30 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
ASTM D256 | ||
-18℃,3.2mm -18℃,3.2mm |
64 | J/m | ASTM D256 |
23℃,3.2mm 23℃,3.2mm |
110 | J/m | ASTM D256 |
落锤冲击 Drop hammer impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.50 mm,所有颜色 1.50 mm, all colors |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
L 级 Level L |
ASTM D785 | ||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus 1 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 1 |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 1 |
|||
断裂 fracture 1 |
% | ASTM D638 | |
弯曲模量 Bending modulus 2 |
MPa | ASTM D790 | |
弯曲强度 bending strength 2 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2.0 in/min |
3 类型 1, 0.050 in/min |
4 10 mil 缺口深度 |
【新闻资讯】查看全部
“小巨人”科亚重新停业究竟意味着什么?
2016-01-15 去年以来,出口订单萎缩,塑料制品与改性专用料滞销,直接影响双螺杆市场走向,不过在一片低迷中,2016年1月9日,科亚装备集团在南京举行隆重开业庆典。这家中国双螺杆挤出行业的“小巨人”在2010年重新创建后再次进行企业重大变革。 科亚的4个重要时刻 1993年,科亚成立于南京,开启中国同向双螺杆挤出机企业制造先河。如今南京已成为中国双螺杆挤出设备的重要生产基地,到2003年科亚发展成为资产上亿元人民币、国内第一的双螺杆企业。 2004年,科亚与 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |