牌号简介 About |
---|
PRIMACOR™ 1321 共聚物是一种乙烯丙烯酸共聚物,适用于挤出吹塑和流延薄膜。 PRIMACOR 1321 共聚物专门用作复合薄膜中的粘结剂层或是软质包转结构中的密封剂层。 PRIMACOR 1321 共聚物具有以下特性: 与PE和PA具有很好的层间粘合力 良好的光学性能 优异的韧性和强度 优异的耐环境应力开裂性能和耐包装内容物性能 良好的热粘性能和热封性能 对水分不敏感 应用领域: 多层复合材料 食品包装 符合以下法规要求: 美国食品和药品管理局 U.S. FDA 21 CFR 177.1310(a)(1) 欧盟(EU) No 10/2011 请查阅法规以获取详尽资料。 PRIMACOR™ 1321 Copolymer is an ethylene acrylic acid copolymer suitable for extruded blown and cast film. PRIMACOR 1321 Copolymer has been specifically designed for use as an adhesive layer in composite films or sealant layer in flexible packaging structures. PRIMACOR 1321 Copolymer exhibits: Good interlayer adhesion to PE and PA Good optical properties Excellent toughness and strength Excellent environmental stress crack and product resistance Good hot-tack and sealability Insensitivity to moisture Applications: Multilayer films Food packaging Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.935 | g/cm³ | ASTM D792 , ISO 1183/A |
熔体质量流动速率 Melt Flow Rate 2 |
|||
190℃,2.16kg 190℃,2.16kg 2 |
2.6 | g/10min | ASTM D1238,ISO 1133 |
共聚单体含量 Co monomer content 3 |
6.5 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding 4 |
10.0 | MPa | ASTM D638 |
屈服,模压成型 Yield, molding |
10.0 | MPa | ISO 527-2/508 |
断裂,模压成型 Fracture, molded 4 |
MPa | ASTM D638 | |
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2/508 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded 4 |
% | ASTM D638 | |
断裂,模压成型 Fracture, molded |
% | ISO 527-2/508 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ISO 527-3 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ISO 527-3 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 , ISO 527-3 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 , ISO 527-3 | |
拉伸应变 Tensile strain |
ASTM D882 , ISO 527-3 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 , ISO 527-3 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 , ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709B , ISO 7765-1/B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 5 |
|||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
MD:51 µm MD:51 µm |
N | ISO 6383-2 | |
TD:51 µm TD:51 µm |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 , ISO 306 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ISO 14782 | |
50.8 µm 50.8 µm |
% | ASTM D1003 |
备注 |
---|
2 如同在生产时测量的一样。 |
3 通过 Dow 属性方法测量的共聚单体含量,和 ASTM D 4094 相比具有相同的精确性。 |
4 510 mm/min |
5 通过 DOW 属性方法测量的共聚单体含量,和 ASTM D 4094 相比具有相同的精确性。 |
【新闻资讯】查看全部
化销华中首次进军可降解塑料市场
2021-10-28 搜料网资讯: 化销华中响应国家环保号召,积极践行央企社会责任,深耕环保领域,于10月首次售出10.4吨生物树脂TH801(PBAT),成功进军可降解塑料市场,在可降解材料领域实现新突破 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |