牌号简介 About |
---|
用于电线和电缆应用中评估的非卤化阻燃柔性Noryl树脂,能够满足UL 1581规定的VW-1和105°C最终使用温度要求。采用标准挤出设备,加工性能好。使用0.12 mm x 20绞合铜导线对2.0 mm电线进行UL1581试验。 Non-Halogenated flame retardant, flexible NORYL resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL 1581. Good processing performance by using standard extrusion equipment. UL1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
10 | g/10min | ASTM D1238 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength |
13 | kN/m | ISO 6383 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -40.0 | ℃ | ASTM D746 |
UL温度额定值 UL temperature rating 7 |
105 | ℃ | UL 1581 |
Heat Deformation(121℃) Heat Deformation(121℃) 8 |
% | UL 1581 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
相对电容率 Relative permittivity |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
6.00 mm 6.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
VW-1 VW-1 2 |
UL 1581 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,30 秒 Shore A, 30 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | UL 1581 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 4 |
MPa | UL 1581 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
% | UL 1581 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 5 |
% | UL 1581 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 6 |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
3. 类型 1, 50 mm/min |
4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
6. 13 mm/min |
7. 2.0mm wire with 0.12 mm x 20 stranded copper |
8. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
【新闻资讯】查看全部
石墨烯又添生态功用:氧化石墨烯土壤菌落更多样化
2015-11-24 当土壤暴露于氧化石墨烯上的时候,其细菌种类也会变得多样化。这项中国科学家的发现表明氧化石墨烯除了在环保方面有重要应用以外,在生态方面也有重要影响。 氧化石墨烯表面丰富的氧含量使得其在电子和纳米产品方面具有非常重要的潜力。土壤生态系统将有可能首次体验到纳米材料的污染,之前关于氧化石墨烯的研究工作也主要集中于纯的菌落,而土壤显然是一种更加复杂的媒介,具有不同的菌落,因此需要更加详细的研究。如今南开大学的Xiangang Hu 和 Qixing Zhou带领的研究团队通过高通量测 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |