牌号简介 About |
---|
NHU-PPA聚合物是一种高温尼龙树脂(聚酰胺),具有高韧性和优异的摩擦阻力。良好的熔体流动性提高了注塑加工性能,耐化学药品,机械强度优异。 NHU-PPA N201 NHU-PPA Polymer is a polyamide-class high temperature nylon resin with high distortion temperature, excellent tenacity and frictional resistance. Featuring good melt flow rate, PPA resin boasts excellent injection molding processibility, acid, alkali and general chemical resistance as well as outstanding mechanical strength. NHU-PPA N201 NHU-PPA Polymer is a polyamide-class high temperature nylon resin with high distortion temperature, excellent tenacity and frictional resistance. Featuring good melt flow rate, PPA resin boasts excellent injection molding processibility, acid, alkali and general chemical resistance as well as outstanding mechanical strength. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
粘数 Viscosity number |
90.0 | cm³/g | ISO 307 |
含水量 water content 2 |
< 0.35 | % | |
灰份含量 Ash Content |
|||
750℃ 750℃ |
0.25 | % | ISO 3451 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
100 | ℃ | ISO 11357-2 |
熔融温度 Melting temperature |
323 | ℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.3 hour |
【新闻资讯】查看全部
挤压模具形成大帽的缘由
2016-08-03 挤压模具时我们会发现,常会有大帽的发生,导致这样缺陷大发生,一般都是模面不平导致剪切不净,在挤压时,铝在进行逐步向外粘连后而造成的,太空模具网根据了解,告诉大家导致挤压模具造成大帽的原因都有哪些。 1、挤压模具端面不平或有缺损口使锁紧面有缝隙,铝窜流。模具缺损口要及时补焊,模面一定要铣平。 2、进料腔外接圆太大(模距过短),模筒锁紧面积就小------进料腔外接圆同筒壁距离正常留单边10mm 极限不少于5mm,挤压比过高的模具不要简单地只用扩大分流腔的办法来 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |