Ixef BXT-2000/0203树脂专用于挤出和吹塑加工。与其它专门针对注射成型牌号不同, Ixef BXT-2000/0203树脂可成功地挤出成管件、管材、片材、膜,以及吹塑成各种型材。 BXT-2000/0203树脂能成功耐受大多数汽车流体和燃料渗透性。同时具有低吸湿性、良好的尺寸稳定性和耐化学性,以及优异的机械性能。 - 本色: Ixef BXT-2000/0203 Ixef® BXT 2000-0203 resin was developed specifically for extrusion and blow-molding processes. Unlike grades targeted for injection molding, Ixef® BXT 2000-0203 resin can be successfully extruded into tube, pipe, sheet and film and blow-molded into various profiles. BXT 2000-0203 resin has proven permeation resistance to most automotive fluids and fuels. It also offers low moisture absorption, excellent dimensional stability, and chemical resistance as well as outstanding mechanical properties. Natural: Ixef® BXT 2000-0203 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 | g/cm³ | ASTM D1895B |
Melt Flow(240℃) Melt Flow(240℃) |
6.00 | g/10 min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2470 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
39.9 | MPa | ASTM D638 |
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2 | |
Modulus of Elasticity Modulus of Elasticity |
GPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Permeation - CE 10 Fuel(60℃) Permeation - CE 10 Fuel(60℃) |
g·mm/m²/atm/24 hr | SAE J2659 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4812 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
拥抱3.0时代 环保企业完成弯道超车的五小气向
2018-02-06 一系列政策春风和现实需求推动我国环境产业进入3.0时代:将绿色融入中国未来的发展,同时,将环保作为促进中国经济转型、推动产业升级的核心力量。从单一设备项目到系统环境治理,再到追求精准治理成效的新时代,走过30余年的环保产业正在迎来新的拐点。 近年来,在“两山论”、“生态文明建设”的大背景下,整体环境质量改善对我国环境治理工作提出了面向效果的更高要求。“十九大”后,生态文明达到新高度,环保制度趋严、趋常态、趋长效,一系列政策春风和现实需求推动我国环境产业进入3.0时代:将绿色 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |