牌号简介 About |
---|
Ultrathene® UE624000是一种具有优异柔韧性和低温性能的EVA共聚物。用户可选择UE624000用于中厚膜应用以及注塑和吹塑。 Ultrathene UE624000 is an EVA copolymer with excellent flexibility and low temperature properties. UE624000 is selected by customers for use in medium to heavy gauge film applications as well as injection and blow molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.1 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
18.0 | wt% | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
91 | ASTM D2240 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD 1% secant, MD |
51.7 | MPa | ASTM D882 |
1% 正割,TD 1% secant, TD |
59.3 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服 MD, yield |
% | ASTM D882 | |
TD,屈服 TD, yield |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm 38 µm |
g | ASTM D1709 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
万华“气垫”专属资料,您爱不释脚的“伴履”
2017-03-27 ――万华化学Wanthane®1495RVTPU 满足您的鞋材需求 “3.15”晚会上曝光的“气垫门”事件让气垫一时间成为新热点。 在商场选鞋时,为什么有那么多人如此看重一块小小的气垫?它 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |