牌号简介 About |
---|
Exceed™ 3812CB是一种茂金属乙烯-己烯共聚物。由Exceed™ 3812CB制成的薄膜具有优异的韧性、冲击强度和穿透性。这些优越的强度特性使其成为一种用途广泛的包装薄膜树脂,非常适合拉伸薄膜。也可用于提高花状熔体指数材料的密封性。 Exceed 3812CB is an ethylene 1-hexene copolymer. Films made from Exceed 3812CB have outstanding toughness, impact strength, and puncture. These superior strength properties make this a very versatile packaging film resin and ideally suited for stretch film. It can also be used to enhance the sealing caulkability of lower melt index materials. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.8 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
1% 正割,TD 1% secant, TD |
96.8 | MPa | ASTM D882 |
1% 正割,MD 1% secant, MD |
87.0 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂 TD, fracture |
43.5 | MPa | ASTM D882 |
TD,屈服 TD, yield |
4.50 | MPa | ASTM D882 |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
MD,屈服 MD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂 TD, fracture |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 6 |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD TD |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Dart Head Type C |
【新闻资讯】查看全部
【干货】液态硅胶LSR成型模具的特点
2021-03-02 搜料网资讯: 热固性液态硅橡胶(LSR)注压模具的结构,总的来说跟热塑性胶料所用的模具结构相似,但也有不少显著差别。例如,LSR胶料一般粘度较低,因而充模时间很短,即使在很低 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |