牌号简介 About |
---|
QC-8740是一种乙烯基酯基片状模塑料(SMC),设计用于需要韧性和阻燃性的部件的压缩成型。它符合许多商业和军事规范的要求。 QC-8740 is a vinyl ester based sheet molding compound (SMC) designed for compression molding of components requiring toughness and flame retardance. It meets the requirements for a number of commercial and military specifications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.90 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.10 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.30 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
214 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
13800 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
贮藏期限 Storage period |
|||
24℃ 24℃ |
wk | ||
脱模时间 stripping time |
|||
149℃ 149℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
上海扩大复工,巴斯夫产能恢复至70%!猴痘病毒突现多国拉警报
2022-05-23 上海进入扩大复工复产阶段 5月22日,浦东新区企业复工复产持续推进,截至目前,在生产重点企业已超1100家,在厂总人数约13.8万人。 据浦东新区科经委介绍,目前,浦东新区已有20 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |