牌号简介 About |
---|
ADSINT TPU 80(热塑性聚氨酯)是为SLS技术开发的一种软质工程白粉。与其他为SLS开发的TPU相比,它的硬度较低。其独特的特点是很高的延伸率,优良的物理性能与橡胶般的弹性和良好的耐磨性以及耐化学腐蚀性相结合。典型的应用包括鞋底、设计服装、整形模型、软管、管子、密封件和轮子。印刷部件的表面非常光滑。ADSINT TPU 80可用于3D系统机器。将提供打印参数。由于印刷温度较低(低于100°C),因此可以节省能源和时间。回收率100%意味着高成本优势。 AdSint® TPU 80 (thermoplastic Polyurethane) is a soft engineered white powder developed for the SLS technology. In comparison to other TPU developed for SLS, it has a lower hardness. Its unique characteristics are very high elongation, excellent physical properties combined with a rubber-like elasticity and a good abrasive as well as chemical resistance. Typical applications are shoe soles, designer clothes, orthopedic models, hoses, tubes, sealings and wheels. The printed parts deliver a very smooth surface. AdSint® TPU 80 can be used on 3D Systems machines. Parameters for printing will be provided. Due to its lower printing temperature (below 100°C), energy and time savings are possible. The recycling rate of 100% implies a high cost advantage. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 到 1.15 | g/cm³ | ISO 61 |
表观密度 Apparent density 2 |
0.55 | g/cm³ | ISO 1068 |
平均颗粒尺寸 Average particle size |
|||
X50 X50 |
56 | µm | ISO 13320 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 , 4 |
|||
断裂 fracture 3 , 4 |
17.0 | MPa | ASTM D412 |
拉伸应变 Tensile strain 3 , 4 |
|||
断裂 fracture 3 , 4 |
600 | % | ASTM D412 |
压缩形变 Compression deformation |
|||
23℃,72 hr 23℃,72 hr |
% | ||
70℃,22 hr 70℃,22 hr |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,20℃ Shore A, 20 ℃ |
ISO 868 | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
抗磨损性 abrasion resistance |
mm³ | ISO 4649 |
备注 |
---|
2. Packed |
3. C 模具 |
4. X Direction |
【新闻资讯】查看全部
合理的模具构造设计打造最佳的模具功能
2016-07-22 良好的铸件结构设计,铸件壁厚尽可能均匀,避免产生热节,以减少模具局部热量集中产生的热疲劳。铸件的转角处应有适当的铸造圆角,以避免模具上有尖角位导致应力产生。 合理的模具结构设计 1)模具中各元件应有足够的刚度、强度,以承受压力而不变形。模具壁厚要足够,才能减少变形。 2)浇注系统设计尽量减少对型芯冲击、冲蚀。 3)正确选择各元件的公差配合和表面粗糙度。 4)保持模具热平衡。 3.规范热处理工艺< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |