牌号简介 About |
---|
单组分聚氨酯树脂聚氨酯膜是将树脂涂在基体上并干燥以充分蒸发溶剂而制成的。该膜给人柔软的手感和干燥的表面,并提供防水和防风性能。采用单组分聚氨酯树脂单独配以适当的交联剂进行固纱,干燥后充分蒸发溶剂,可形成高粘纱膜。鞋、皮包、成衣耐阻塞、耐水性高、手感好、防水软树脂。具有优异的聚氨酯或聚氯乙烯粘合强度、耐候性、耐水压性和抗阻塞性。 One component PU Resins PU membrane is produced by coating the resin on substrate and drying it to vaporize the solvent adequately. The membrane gives soft hand-feel and dry surface, and offers waterproof and windproof properties. Using one component type PU resin alone with adequate crosslinker for yarn fixation, following by drying process to vaporize solvent adequately, could form high yarn-bonding membrane. Shoes, leather bag, ready-make clothes Blocking resistance, high water resistance, good hand-feel Waterproof soft resin. Excellent adhesive strength with PU or PVC, weather resistance, water pressure resistance, and blocking resistance |
技术参数 Technical Data | |||
---|---|---|---|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
溶剂 solvent |
DMF/TOL | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
Clear/Transparent Colorless Clear, Light Yellow | ||
固体含量 Solid content |
27 到 29 | % | |
粘度 viscosity |
|||
25℃ 25℃ |
50 到 80 | Pa·s | |
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
100% 正割 100% secant |
1.96 到 3.92 | MPa | |
拉伸强度 tensile strength |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
改性配混需求不停的调整物料工艺
2019-01-25 作为改性配混工厂管理者,需要不停的调整物料工艺,计划不同产线的产能。如果管理者被大量生产和设备运行数据包围,而不能有效管理原材料需求计划及工厂排产计划,最终将缺乏准确、及时的生产数据作为决策支撑,无法满足企业对精细化生产和管控的需求,以至于工厂效率低下,缺乏竞争力。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |