牌号简介 About |
---|
lnp stat-loy A30009化合物lnp stat-loy A30009是基于abs的化合物。这种材料的附加特性包括:抗静电、阻燃。又名:lnp*stat-loy*化合物A-fr产品再订购名称:A30009lnp-loy A30009化合物lnp-stat-loy A30009是一种基于含有阻燃剂的丙烯腈-丁二烯-苯乙烯树脂的化合物。这种材料的附加特性包括:抗静电、阻燃。又名:LNP*STAT-LOY*化合物A-FR产品再订购名称:A30009LNP STAT-LOY A30009化合物LNP*STAT-LOY*A30009是一种基于丙烯腈-丁二烯树脂的化合物,含有专有填料、阻燃剂。附加功能包括:永久抗静电,阻燃。又名:lnp*stat-loy*化合物a-fr产品再订购名称:A30009 LNP STAT-LOY A30009 is a compound based on ABS. Added features of this material include: Antistatic, Flame Retardant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.21 | g/cm³ | ASTM D792 |
密度 Density |
1.21 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:24 hrs TD:24 hrs |
0.80 to 1.0 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
0.70 to 0.90 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
0.88 | % | ISO 294-4 |
MD:24 hrs MD:24 hrs |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 3 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 3 |
|||
23℃ 23℃ 3 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2,0 in/min |
3 0,079 in/min |
4 Break |
5 80*10*4 |
6 80*10*4 mm |
【新闻资讯】查看全部
3D打印将这样取代模具制造业?
2016-09-14 模具行业是一个跨度最大的行业,它与制造业的各个领域都发生关系。在现代社会,制造和模具是高度依存的,无数产品的部件都要通过模制(注射、吹塑和硅胶)或铸模(熔模、翻砂和旋压)来制造。无论什么应用,制造模具都能在提高效率和利润的同时保证质量。 CNC加工是在制造模具时最常用的技术。虽然它能够提供高度可靠的结果,但同时也非常昂贵和费时。所以很多模具制造企业也开始寻找更加有效的替代方式。而通过增材层制造制作模具也就成了一个更加具有吸引力的方法,特别是因为模具一般都属于小批量生产而且形 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |