牌号简介 About |
---|
EPO-TEK® 353ND-T4是一种双组分、高触变性环氧树脂,具有不流动性和耐高温性。这是EPO-TEK 353ND-T的高粘度版本,适用于需要减少流量的应用。 EPO-TEK® 353ND-T4 is a two component, highly thixotropic epoxy with non-flowing properties and high temperature resistance. This is a higher viscosity version of EPO-TEK® 353ND-T for applications needing decreased flow. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颗粒大小 Particle size |
< 20.0 | µm | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Degradation Temperature Degradation Temperature |
409 | ℃ | TGA |
Die Shear Strength(>15 kg,23℃) Die Shear Strength(>15 kg,23℃) |
35.2 | MPa | |
工作温度 working temperature |
|||
Continuous Continuous |
℃ | ||
Intermittent Intermittent |
℃ | ||
Storage Modulus(23℃) Storage Modulus(23℃) |
GPa | ||
触变指数 Thixotropic index |
|||
加热减量 Heating reduction |
|||
200℃ 200℃ |
% | ||
250℃ 250℃ |
% | ||
300℃ 300℃ |
% | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 6 |
|||
-- -- 7 |
|||
密度 Density |
|||
Part B Part B |
g/cm³ | ||
Part A Part A |
g/cm³ | ||
粘度 viscosity 8 |
|||
23℃ 23℃ 8 |
Pa·s | ||
固化时间 Curing time |
|||
150℃ 150℃ |
hr | ||
储存稳定性 storage stability |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
搭接剪切强度 lap shear strength |
|||
23℃ 23℃ |
MPa | ||
相对电容率 Relative permittivity |
|||
1 kHz 1 kHz |
|||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature 2 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-- -- 3 |
4.3E-5 | cm/cm/℃ | |
-- -- 4 |
2.3E-4 | cm/cm/℃ | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period 5 |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
3 Below Tg |
4 Above Tg |
5 Refrigerated |
6 Part B |
7 Part A |
8 20 rpm |
【新闻资讯】查看全部
科思创:拟用聚氨酯消费转子叶片
2016-09-14 Covestro创新及可持续的材料解决方案提高了风机制造效率,并延长了陆上和海上风电场的使用寿命。 Covestro将在2016年德国塑料橡胶展会(K展)上展示其最新成就。一个例子便是用于制造转子叶片的灌注树脂。当和强化玻璃纤维共同使用时,能缩短生产周期。 Klausen 说“对生产商来说有很大的成本优势,毕竟转子叶片约占到风力涡轮机总成本的四分之一。”这种树脂也有非常良好的机械性能。 用真空注入的工艺,生产过程包括将核心材料和玻璃纤维放置在模具中,再用薄膜 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |