牌号简介 About |
---|
Ultem DT1810EV树脂改善了延展性、透明性、增强流动性的聚醚酰亚胺混合物(TG 200C),具有内部脱模性和增强的延展性。符合环保要求,UL94 V0上市。Ultem DT1810EV树脂改善了延展性、透明性、增强流动性的聚醚酰亚胺混合物(TG 200C),具有内部脱模性和增强的延展性。符合RoHS。UL94 V0上市。 Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.28 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
337℃,6.60kg 337℃,6.60kg |
43 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
360℃,5 kg 360℃,5 kg |
56.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 到 0.70 | % | 内部方法 |
吸水率 Water absorption rate |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
0.36 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 9 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 10 |
|||
23℃ 23℃ 10 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 11 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 12 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D4812 | ||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 13 |
℃ | ISO 75-2/Ae | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ASTM D1525, ISO 306/B50 11 14 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~150℃ MD:-40~150℃ |
1/℃ | ASTM E831 | |
MD:23~150℃ MD:23~150℃ |
1/℃ | ISO 11359-2 | |
TD:-40~150℃ TD:-40~150℃ |
1/℃ | ASTM E831 | |
TD:23~150℃ TD:23~150℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 120*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
陶氏化学斥资20亿美元扩展路易斯安那州业务
2017-11-02 据OGJ网站10月30日休斯敦报道,新成立的杜邦公司的业务部门陶氏杜邦材料科学部门日前向化学投资拨款20亿美元来进一步扩大其在路易斯安那州的石油化工业务。 路易斯安那州经济发展部10月27日在陶氏化学公司在路易斯安那州的3300英亩Plaquemine石化厂施工现场说,与陶氏化学公司先前宣布的在伊贝维尔和西巴吞鲁日涉及建造两个生产下一代合成橡胶和聚乙烯厂的扩建一起,这笔投资还包括旨在提高其在路易斯安那州现有乙烯产能(包括重新启动位于圣查尔斯的一个现有乙烯装置)以及增加100 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |