牌号简介 About |
---|
NGL300IG是一种基于丁烯共单体的线性低密度聚乙烯树脂,由IEPL使用加拿大杜邦(现为Nova Chemicals)的“Sclairtech”溶液聚合工艺生产,用于注塑应用。作为一种共聚物,它具有优异的加工性、抗冲击性、优异的柔韧性和抗翘曲性。 NGL300IG is a Butene co-monomer based Linear Low Density Polyethylene Resin manufactured by IEPL using "SCLAIRTECH" solution polymerisation process of DU Pont, Canada (Now Nova Chemicals) designed for Injection Molding application. As a copolymer it offers excellent processability, impact resistance, outstanding flexibility and warpage resistance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
30 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
11.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
900 | % | ASTM D638 |
弯曲模量 Bending modulus |
325 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
塑料注塑成型为什么起皮?大家一同来剖析
2016-10-27 聚合物在塑胶挤出或注射成型时,在流体剪切速率较低时经口模或浇口挤出物具备润滑的轮廓与平均的形状。当剪切速率或剪切应改性塑料力增进到一定值时,在挤出物外表取得鲜丽且外面邃密精美;当塑胶挤出速度再举高时,挤出物表面将呈现浩繁的不划定规矩的结节、曲解或竹节纹,以至支离和断裂成碎片或柱段,我们称之为”熔体破碎”。 这些现象说明,在低的剪切应力或速度下,各种成分惹起的小扰动被熔体胁制;而在高的剪切应力或速率下,流体中的扰动难以压抑,并进行成不不乱运动;当抵达一个临界剪切力时,将引起流 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |