| 牌号简介 About |
|---|
| “Moplen”RP220M是一种控制流变介质的改性丙烯无规共聚物，用于生产高透明的铸造薄膜。它不含滑动剂或防阻塞剂。它具有良好的加工性、透明度和光泽度，并表现出良好的热焊接性。主要应用于食品包装、文具包装、衬衫包装和丝袜包装。它还适用于生产固定式文件夹。”MOPLEN“RP220M适用于食品接触。有关监管信息，请参阅“MOPLEN”RP220M产品管理公告（PSB）。 "Moplen" RP220M is a controlled rheology medium modified propylene random copolymer for manufacturing high transparent cast films. It contains no slip or antiblocking agents. It offers good processability, excellent clarity and gloss and exhibits very good heat weldability. Main applications are packaging of foodstuffs, packaging of stationary, shirts and hosiery. It is also suitable for production of stationary folders. "Moplen" RP220M is suitable for food contact. For regulatory information please refer to "Moplen" RP220M Product Stewardship Bulletin ( PSB ). |
产品描述 Product Description
用途：薄膜;包装;流延薄膜;食品包装;文具;
加工条件：流延薄膜
性能特点： 可控流变; 焊接; 透光性好; 无规共聚物; 食品接触; 表面光泽度好; 易加工; Excellent Processability,Good Clarity,Good surface appearance,Controllable rheological,Food contact compliance,Random copolymer,Welding
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.900 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
8.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
屈服 yield |
23.0 | MPa | ISO 527-2 |
|
断裂 fracture |
26.0 | MPa | ISO 527-2 |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
屈服 yield |
12 | % | ISO 527-2 |
|
断裂 fracture |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
摩擦系数 friction coefficient |
|||
|
动态，铸造薄膜 Dynamic, cast thin film |
ASTM D1894 | ||
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
µm | ||
|
割线模量 Secant modulus |
|||
|
MD：50 µm，铸造薄膜 MD: 50 µ m, cast thin film 2 |
MPa | ASTM D882 | |
|
MD：50 µm，铸造薄膜 MD: 50 µ m, cast thin film |
MPa | MA 18068 | |
|
TD：50 µm，铸造薄膜 TD: 50 µ m, cast thin film |
MPa | MA 18068 | |
|
拉伸强度 tensile strength 3 |
|||
|
MD，屈服，50 µm，吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | MA 18068 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | MA 18068 | |
|
拉伸应变 Tensile strain 3 |
|||
|
MD，断裂，50 µm，挤塑薄膜 MD, fracture, 50 µ m, extruded film |
% | ASTM D882 | |
|
MD，断裂，50 µm，铸造薄膜 MD, fracture, 50 µ m, cast thin film |
% | MA 18068 | |
|
TD，断裂，50 µm，铸造薄膜 TD, fracture, 50 µ m, cast thin film |
% | MA 18068 | |
|
落锤冲击 Drop hammer impact |
|||
|
铸造薄膜 Casting thin film |
g | MA 17106 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
0℃ 0℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，50.0 µm，铸造薄膜 45 °, 50.0 µ m, cast thin film |
ISO 2813 | ||
|
雾度 Haze |
|||
|
50 µm，铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 1.2 in/min |
| 3 20 in/min |
|
【新闻资讯】查看全部
日本炼油商出光兴产和昭和壳牌签署协作协议
2017-05-11 据路透社东京5月9日消息，日本炼油商出光兴产和昭和壳牌周二表示，双方已经签署一份协议，在出光兴产并购昭和壳牌案停滞不前的情况下建立业务合作关系。 两家公司公告称，根据协议，双方将在原油采购和运输以及生产计划方面采取更加紧密的合作。 去年12月，出光兴产完成了收购昭和壳牌公司不到三分之一股权的交易，但是由于受到来自于出光兴产公司创立家族的反对，两家公司完全合并的目标已经被推迟。 两家公司在公告中称，更加紧密的合作将令两家公司在从2017年4月份 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付