典型应用:高山滑雪靴,无噪音齿轮,传送带PA 12弹性体,聚酰胺弹性体的最重要的一个子类,属于热塑性弹性体(TPE)日益重要的材料类别。由于其优良的性能,在许多应用中是必不可少的。PA 12弹性体是由PA 12段和聚醚段组成的嵌段共聚物。富含PA 12的产品具有PA 12的主要性能,而随着聚醚含量的增加,弹性体特性变得更加明显。也就是说,聚合物变得更灵活,在低温下具有更高的冲击强度。 Typical Applications: alpine ski boots, noiseless gears, conveyor belts PA 12 elastomers, the most important subgroup of polyamide elastomers, belong to the increasingly important material class of thermoplastic elastomers (TPE). Because of their excellent properties, they are indispensable in many applications. PA 12 elastomers are block copolymers consisting of PA 12 segments and polyether segments. PA 12-rich products have the major properties of PA 12, while the elastomer characteristics become more apparent with increasing polyether content. That is the polymers become more flexible, with higher impact strength at cold temperatures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
TD:3.0 mm TD:3.0 mm |
0.90 到 1.4 | % | |
MD:3.0 mm MD:3.0 mm |
0.60 到 1.1 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
1.1 | % | ISO 62 |
粘数 Viscosity number |
190 | cm³/g | ISO 307 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ||
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A | |
-- -- |
℃ | ISO 306/B | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
可燃性等级 Flammability level |
|||
1.6 mm 1.6 mm |
IEC 60695-11-10, -20 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
-- -- |
MPa | ||
50% 应变 50% strain |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
SABIC碳纤复合聚碳酸酯在1毫米厚笔电外壳的开发运用
2020-04-23 SABIC 在最近的一项研究中证明,1 毫米厚的外壳可以满足超薄笔记本电脑或平板电脑的所有相关行业性能规范。 消费电子产品是一个动态市场,产品的迭代周期很短。消费者希望从他们 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |