牌号简介 About |
---|
Technyl A 218G V33 Black 34N是一种聚酰胺66,用33%的玻璃纤维增强,热稳定,用于注塑成型。该产品有黑色可选。 TECHNYL® A 218G V33 Black 34N is a polyamide 66, reinforced with 33% of glass fiber, heat stabilized, for injection moulding. This grade has been specially designed to improve its resistance to automotive cooling liquids, increasing lifetime of parts in permanent contact with such liquids. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.39 | g/cm³ | ISO 1183/A |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
5.3 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
1.7 | % | ISO 62 |
23℃,24hr 23℃,24hr |
0.78 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
11300 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/1A | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
Freeformer喜获李奥纳多•达•芬奇设计大奖…
2016-04-07 近日,意大利工业设计师协会向阿博格颁发李奥纳多•达•芬奇设计大奖(Leonardo da Vinci Design Award),以肯定阿博格Freeformer机器为增材制造提供的创新设计系统所作的贡献。 “我非常高兴能够代表阿博格意大利公司接受此奖。无论是设计还是为塑料加工企业提供的全功能一次性零件和小零件的批量生产选项,阿博格Freeformer都是独一无二的”,总经理Adriano Carminati在颁奖典礼上说。 < |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |