牌号简介 About |
---|
A- 4122 NL AMODEL树脂是22%玻纤增强高反射白色级的聚邻苯二甲酰胺(PPA),主要是为了在水冷模具成型时,获得高结晶度。这种材料具有高耐热性,在宽温度范围内具有高强度和刚度。同时吸湿性低,具有优异的耐化学性和优良的电性能。 快速结晶率和高流动性可能会缩短生产周期,从而提高成型效率,降低部件成本。 - 白色: A-4122 NL WH 905 Amodel® A-4122 NL resin is a 22% glass reinforced, high-reflectivity white grade of polyphthalamide (PPA), designed to provide high crystallinity when molded in water-cooled molds. This material exhibits high heat resistance, high strength and stiffness over a broad temperature range. It also offers low moisture absorption, excellent chemical resistance and excellent electrical properties. Its rapid crystallization rate and high flow can result in short cycles and therefore high molding productivity and lower part cost. White: A-4122 NL WH 905 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.48 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
|||
TD TD |
0.60 | % | ASTM D955 |
MD MD |
0.40 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.24 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
27 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
150 到 250℃ 150 to 250 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
150 到 250℃ 150 to 250 ℃ |
cm/cm/℃ | ASTM E831 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光反射率 Light reflectivity |
% | ASTM E1331 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
生物塑料开展趋向
2017-06-06 二氧化碳的转化每年都发生着显著的变化,二氧化碳是碳氢化合物、碳水化合物和作为生产化学品和聚合物的原料。根据德国赫尔斯特新星研究所“生物基聚合物革命性变化”的新趋势报告,生物基化学品如己二酸,丁二醇,呋喃二甲酸,乳酸和琥珀酸将形成生物基化学平台,到2030年,价值超过300亿欧元。虽然这些化学品在很大程度上用于聚合物生产,但与其他聚合物相关的发展主要集中在可再生原料的使用。 聚乳酸(PLA)已经在S-曲线的早期生长阶段留下了胚胎期,而聚丁二酸丁二醇酯(PBSX)和聚羟基链烷酸 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |