牌号简介 About |
---|
NGL015FS是IEPL利用加拿大杜邦的“SCLARTECH”溶液聚合工艺生产的一种基于丁烯共聚单体的低密度聚乙烯树脂(现为Nova Chemicals),提供窄分子量分布共聚物和滑脱防堵添加剂,专为生产高强度吹塑而设计。适用于多层和衬里应用的各种厚度的薄膜。 NGL015FS is a Butene Co-monomer based Liner Low Density Polyethylene Resin manufactured by IEPL using "SCLAIRTECH" solution polymerisation process of DU Pont, Canada (Now Nova Chemicals) offers narrow molecular weight distribution copolymer with slip & antiblock additive which has been specifically designed for the production of high strength blown film of various thickness for multilayer & liners application. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
12.0 | MPa | ASTM D882 |
TD,屈服 TD, yield |
11.5 | MPa | ASTM D882 |
MD,断裂 MD, fracture |
28.0 | MPa | ASTM D882 |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
kN/m | ASTM D1709 | |
撕裂强度 tear strength |
ASTM D1922 | ||
MD MD |
kN/m | ASTM D1922 | |
TD TD |
kN/m | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美媒:丰田追加投资 扩大在美电动车零部件生产
2022-02-14 据美联社美国西弗吉尼亚州布法罗2月11日报道,丰田汽车公司11日宣布,将投资9000万美元,进一步扩大在美国西弗吉尼亚州和田纳西州的电动汽车零部件生产。 报道称,三个月前,这家 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |