牌号简介 About |
---|
利安德巴塞尔澳大利亚的HP744T是一种高熔体流动,反应堆外有核均聚物。HP744T具有很高的硬度、很低的感官性能和改进的抗虎纹性能。HP744T是为汽车、化合和薄壁注塑应用而设计的,在这些应用中,要求快速的循环时间、一致的性能和平衡的机械性能水平。 LyondellBasell Australia's HP744T is a high melt flow, ex-reactor nucleated homopolymer. HP744T has high stiffness, very low organoleptic properties and improved anti-tiger stripe performance. HP744T has been formulated for use in automotive, compounding and thin wall injection moulding applications, where rapid cycle times are required together with consistent performance and a balanced level of mechanical properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
70 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
2.0 | kJ/m² | ISO 180-1A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
105 | ℃ | ISO 75-2/B |
维卡软化温度 Vicat Softening Temp |
151 | ℃ | ISO 306 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
CMS结合Fraunhofer开发首个混合热塑性3D打印零碎
2017-09-25 近日,意大利加工制造专家CMS宣布了与Fraunhofer机床及成型技术研究所(Fraunhofer IWU)的合作关系,他们将共同开发用于3D打印、加工热塑性复合材料部件的复合系统――CMS Kreator。 人们广泛认为3D打印与其他制造工艺的结合,可以大大发挥出3D打印自身的全部潜力。因此许多公司都在着手开发混合制造系统,它结合加、减两种制造系统,来制作出高强度的复杂部件,同时保证制作出的成品表面光滑、专业。 虽然这一做法在金属增材制造行业并不少见,但 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |