牌号简介 About |
---|
Nucrel® 0908HS是一种乙烯-甲基丙烯酸共聚物树脂,通常由9 wt%甲基丙烯酸制成。该树脂可用于传统的挤出涂层、共挤涂层以及设计用于加工聚乙烯树脂的铸膜操作。 Nucrel® 0908HS is an ethylene-methacrylic acid copolymer resin, made with nominally 9 wt% methacrylic acid. The resin is available for use in conventional extrusion coating, coextrusion coating, and cast film operations designed to process polyethylene resins. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ASTM D792 |
密度 Density |
0.930 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
8.0 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
8.0 | g/10min | ISO 1133 |
Methacrylic Acid Content Methacrylic Acid Content |
9.2 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
冰点 freezing point |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
Bunzl将收购土耳其塑料包装公司Bursa
2021-04-01 搜料网资讯: 在2月29日的一个新闻发布会上,Bunzl表示其收购了加利福尼亚州的Earthwise Bag Co.、巴西的一家牙科产品供应商Dental Sorria Ltda.,并且将要收购一家土耳其的塑料包装公司Burs |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |