牌号简介 About |
---|
SABIC® LDPE 2201H0W是一个没有添加剂的等级,具有很好的下拉能力。基于2201TH00的薄膜结合了韧性、高撕裂强度和良好的光学性能。应用SABIC® LDPE 2201H0W通常用于需要良好光学性能的薄膜包装。由于迁移水平非常低,SABIC® LDPE 2201H0W通常可用于食品应用。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LDPE 2201H0W is a grade without additives with a very good draw down ability. Films based on 2201TH00 combine toughness with high tear strength and very good optical properties. Application SABIC® LDPE 2201H0W is typically used for thin packaging film purposes, where good optical properties are required. SABIC® LDPE 2201H0W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.85 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
1.0 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
170 | MPa | |
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ||
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ||
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁冲击强度 Izod notched impact strength |
|||
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻塞力 Blocking force |
|||
吹塑薄膜,50.0 µm Blow molded film, 50.0 µ m |
g | 内部方法 | |
Re-blocking - 吹塑薄膜(50.0 µm) Re blocking - blow molded film (50.0 µ m) |
g | 内部方法 | |
撕裂强度 tear strength 1 |
ISO 6383-2 | ||
MD,50 µm MD,50 µm |
kN/m | ||
TD,50 µm TD,50 µm |
kN/m | ||
memo_intro memo_intro |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部 ![]()
印尼拟启动22个新石化项目
2022-01-11 搜料网资讯: 近日,数据分析公司GlobalData表示,到2025年前,受塑料和化肥强劲需求的推动,印度尼西亚将启动22个新石化项目。GlobalData的最新报告显示,预计在印尼开始运营的22个石化 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |