牌号简介 About |
---|
这一等级结合了非常高的冲击强度,即使在低温下,具有高刚度和中等流动特性。适用于高负荷、高韧性的工业部件和容器的注塑成型。它也适用于挤压应用,如薄板、瓦楞纸板和型材。它也可以在紫外线稳定版本。本文所述产品尤其未经测试,因此未经验证可用于医药/医疗应用。 This grade combines a very high impact strength, even at low temperatures, with a high stiffness and moderate flow properties. It is suitable for injection moulding of technical components and containers exposed to heavy loads and needing a high toughness. It is also suitable for extrusion applications like thin sheet, corrugated board and profiles. It is also available in an UV-stabilized version. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
1.8 | g/10min | ASTM D1238,ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃ -20℃ |
10 | kJ/m² | ISO 179/1eA |
0℃ 0℃ |
40 | kJ/m² | ISO 179/1eA |
23℃ 23℃ |
75 | kJ/m² | ISO 179/1eA |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-20℃ -20℃ |
J/m | ASTM D256-A | |
0℃ 0℃ |
ASTM D256A , ISO 180/1A | ||
23℃ 23℃ |
ASTM D256A , ISO 180/1A | ||
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 4 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 5 , ISO 306/A120 5 | |
B120 B120 |
℃ | ASTM D1525 6 , ISO 306/B120 6 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
1% 正割 1% secant 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/1A/50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 2.0 in/min |
4 testbar 80*10*4mm |
5 标准 B (120°C/h), 压 力1 (10N) |
6 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
2018国际汽车工程技术展览会将在重庆召开
2018-04-16 由沃森展览联合权威单位共同组织的2018重庆国际汽车工程技术展览会(AEE)将于2018年9月20-22日在重庆国际博览中心举办,展品覆盖汽车前瞻技术、新能源汽车工程、汽车材料、汽车焊装、汽车涂装、汽车零部件加工、汽车关键零部件等,组委会利用优质的资源积极邀请诸如长安、长安福特、长安铃木、吉利汽车、长城汽车、上汽、上汽通用、东风、力帆、北京现代、奇瑞、广汽、神龙、比亚迪、一汽、一汽大众、一汽丰田、博世、大陆、麦格纳、天纳克等汽车主机厂和零部件制造商采购、技术研发工程师参加展会。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |