牌号简介 About |
---|
AOC的VipelF282系列树脂是高分子量、双酚A富马酸、不饱和聚酯树脂。VIPEL F228系列具有优良的保质期,是理想的纤维缠绕和喷涂应用。其中一个独特的版本是Vipel F282-ZZZ-00,这是一种粉末状醇酸产品,可以运往国外,并在当地与苯乙烯和其他单体混合。更多信息请参见Vipel F282-ZZZ-00产品数据表。优点耐腐蚀AOC的VipelF282设计用于制造各种化学环境的零件,如酸性、漂白剂、过氧化氢、氧化介质和腐蚀性。有关耐腐蚀性信息,请参阅AOC的“耐腐蚀树脂指南”。有关树脂是否适合任何特定化学环境的问题,请联系AOC代表。用途广泛,适用于手工制作、喷涂、纤维缠绕等多种制造方法。制造商有责任确保最终的复合材料得到良好的固化。用于FDA应用的所有复合材料应在180°F/82°C下至少固化4小时。固化后,应使用肥皂和水清洗层压板,然后冲洗。绕组等。 AOC's Vipel F282 series resins are high molecular weight, bisphenol-A fumarate, unsaturated polyester resins. Vipel F282 series has an excellent shelf life and is ideal for filament winding and spray-up applications. One unique version is Vipel F282-ZZZ-00 which is the powdered alkyd product that can be shipped abroad and blended locally with styrene and other monomers. Please see the Vipel F282-ZZZ-00 product data sheet for additional information. BENEFITS Corrosion Resistance AOC's Vipel F282 is designed to make parts for a broad range of chemical environments such as acidic, bleach, hydrogen peroxide, oxidizing media and caustic. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information. For questions regarding suitability of a resin to any particular chemical environment contact your AOC representative. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up and filament winding. It is the fabricator's responsibility to be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F/82°C for at least 4 hours. After post curing, laminate should be washed with soap and water and then rinsed. winding, etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
50 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3030 | MPa | ASTM D638 |
拉伸强度 tensile strength |
70.3 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.6 | % | ASTM D638 |
弯曲模量 Bending modulus |
3030 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
min | ||
放热峰值 exothermic peak |
℃ | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 LV Brookfield LV |
Pa·s | ||
胶凝时间 Gelation time |
|||
82℃ 82℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫:路德维希的TDI消费线正在消费“碰运气”资料
2017-05-31 虽然之前路德维希巴斯夫旗下新设的TDI工厂在商业运作上一直困难重重,但其已于5月中旬起开始运行。一名发言人在接受Plasteurope.com采访时证实了“碰运气”材料现已上线生产。 尽管新发故障已修复、工厂重启运行,但由于Antwerp的光气反应器作为替代品,无法满足起初该工厂设定的产出要求,因此这条300,000吨/年产能生产线的产出仍在下滑。此位发言人并未透露产能的具体减少程度。 新反应器计划于明年送达工厂。预期此次装配过程中还会多次遭遇停工问题,但供 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |