牌号简介 About |
---|
建议在注塑工艺中使用repol h200mk。它是一种理想的材料用于成型注射器和清晰的刚性物品复杂,长流程和多腔成型。repol h200mk含有澄清剂和抗静电剂,可减少产品上积聚的静电。根据USP XXIX和IP96,repol h200mk使用四种不同的萃取剂进行系统和皮内测试。该等级还符合E.P.的过度毒性试验和I.S.的皮肤刺激试验。 Repol H200MK is recommended for use in Injection Moulding processes. It is an ideal material to use in moulding syringes and clear rigid articles with intricate, long flow paths and multicavity moulding. Repol H200MK contains clarifier and antistatic agent that reduces static charge build up on products. Repol H200MK complies with the systemic and intracutaneous tests with four different extractants as per USP XXIX and IP96. The grade also complies with undue toxicity test as per E.P. and skin irritation test as per I.S. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
20 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服,注塑成型 Yield, injection molding 2 |
35.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
屈服,注塑成型 Yield, injection molding 2 |
11 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
1% 正割,注塑成型 1% cut, injection molding |
1700 | MPa | ASTM D790-A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,注塑成型 23 ℃, injection molding |
26 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2.0 in/min |
【新闻资讯】查看全部
由回收的PET和聚氨酯胶粘剂制成的复合材料,用于阻隔噪音
2022-01-14 搜料网资讯: 哥伦比亚的一个科学家小组已经开发出一种由废旧塑料制成的用于阻隔噪音的新材料,其中采用了聚氨酯胶粘剂。 Henry Colorado和安提奥基亚大学工程系复合材料实验室的团 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |