牌号简介 About |
---|
Viton® B-600氟弹性体是一种胶聚合物,具有改进的三元共聚物加工工艺和较低的化合物粘度,以及“B族”氟橡胶优异的耐热和耐流体特性。Viton® B-600特别适用于双酚体系的固化:氟橡胶固化剂20号和30号或氟橡胶固化剂50号。与Viton B相比,Viton® B-600提供:改进的压缩成型增加模具流动更容易模具释放改进的挤压和压延提高固化率改进的压缩变形阻力应用Viton® B-600强烈推荐用于以下应用:模制品,例如轴密封压延制品,例如烟道膨胀节。 Viton® B-600 fluoroelastomer is a gum polymer that demonstrates improved terpolymer processing and lower compound viscosity, along with the excellent heat and fluid resistance characteristics of the "B-family" of Viton®. Viton® B-600 is especially suited to curing with the bisphenol system: Viton® Curative No. 20 and No. 30 or Viton® Curative No. 50. Compared to Viton® B, Viton® B-600 provides: Improved compression molding increased mold flow easier mold release Improved extrusion and calendering Increased cure rate Improved compression set resistance Applications Viton® B-600 is highly recommended for applications like: Molded goods, e.g., shaft seals Calendered goods, e.g., flue duct expansion joints |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.85 | g/cm³ | ASTM D792 |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
65 | MU | ASTM D1646 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 2 |
68 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 3 |
74 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 4 |
71 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变,23℃ 100% strain, 23 ℃ 5 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 6 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 7 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服,23℃ Yield, 23 ℃ 5 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 6 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 7 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂,23℃ Fracture, 23 ℃ 5 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 6 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 7 |
% | ASTM D412 | |
压缩形变 Compression deformation |
ASTM D395B | ||
200℃,22 hr 200℃,22 hr |
% | ASTM D395B | |
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积变化 Volume change |
ASTM D471 | ||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
150℃,70 hr,in Sulfuric Acid 96% 150℃,70 hr,in Sulfuric Acid 96% |
% | ASTM D471 | |
175℃,70 hr,在Stauffer 7700 液体中 175 ℃, 70 hr, in Stauffer 7700 liquid |
% | ASTM D471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20 in/min, 老化 Sulfuric Acid 96% 70 hr 在 302°F |
3 20 in/min, 老化 24 hr 在 450°F |
4 20 in/min, 老化 70 hr 在 527°F |
5 老化 Sulfuric Acid 96% 70 hr 在 302°F |
6 老化 24 hr 在 450°F |
7 老化 70 hr 在 527°F |
【新闻资讯】查看全部
江山化工:转型聚碳酸酯,业绩反转
2016-01-11 DMF龙头,转型聚碳酸酯。江山化工现有DMF产能16万吨、DMAC产能4万吨、顺酐及衍生物产能8万吨,是全球最大的DMF生产企业之一,国内规模第二,市场占有率25%,是中国最大的 DMAC生产企业,规模第一,市场占有率65%。浙铁集团12月4日公告拟注入旗下优质资产浙铁大风。重组完成后,聚碳酸酯将成为公司核心主业。 聚碳酸酯前景广阔。聚碳酸酯主要应用于电子电器、建筑和汽车,2005年至今中国消费增速12%,拜耳预计未来6年全球聚碳酸酯需求增速4.6%, 提高3PCT。技术门 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |