牌号简介 About |
---|
PRE-ELEC® PP 1351是一种基于聚丙烯的耗散热塑性化合物。通过使用特殊的导电碳黑来实现电损耗。除了10e5-10e8欧姆之间的稳定表面电阻。PRE-ELEC® PP 1351具有良好的机械性能平衡,易于注射成型。典型应用包括注塑耗散静电放电产品,如板条箱、盒子和手提箱。 PRE-ELEC® PP 1351 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resistance between 10e5-10e8 ohms. PRE-ELEC® PP 1351 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded dissipative ESD products such as crates, boxes and tote bins. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.996 | g/cm³ | ASTM D792 |
密度 Density |
0.990 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
230℃,2.16kg 230℃,2.16kg |
6.0 | g/10min | ISO 1133 |
230℃,5.0kg 230℃,5.0kg |
28 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
1.2 to 1.8 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
4 mm 4 mm |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,4 mm Fracture, 4 mm |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
4 mm 4 mm |
MPa | ISO 178 | |
4 mm 4 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 2 |
|||
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ASTM D256 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 2 |
|||
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
ISO 179 | ||
23℃ 23℃ |
ASTM D256 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
ISO 180 | ||
Area Area |
ASTM D256 | ||
-20℃,4.00 mm -20℃,4.00 mm |
kJ/m² | ASTM D256 | |
23℃,4.00 mm 23℃,4.00 mm |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
-20℃,4 mm -20℃,4 mm |
kJ/m² | ASTM D256 | |
23℃,4 mm 23℃,4 mm |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 2 |
ISO 180 | ||
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 3 | |
-- -- |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4 mm thickness |
3 标准 B (120°C/h), 载荷2 (50N) |
4 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
罗杰斯发布聚氨酯防水资料家族新成员薄型AquaPro 37
2017-06-21 罗杰斯公司(Rogers Corporation)高弹体材料解决方案事业部近日发布了一款新产品 -- 薄型AquaPro® 37™(AquaPro® 37™ Thin),进一步扩大了AquaPro® 37™泡棉系列的厚度范围,这种材料可为敏感电子元件和器件密封提供长期可靠性保护。 罗杰斯高弹体材料解决方案事业部专注于在多种应用中提供高性能工程材料解决方案,其著名的PORON®聚氨酯泡沫具有优秀的抗压缩形变,持久的密封和缓冲性能以及良好的耐化学品性。AquaPro® 37™系 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |