牌号简介 About |
---|
这种高密度聚乙烯是一种乙烯-己烯共聚物,为吹塑薄膜应用量身定制,需要:高硬度、优异的薄膜拉伸性能、与LLDPE和LDPE混合的特殊加工性能、典型的吹塑薄膜应用包括:概念袋和微纳袋、多壁衬里、共挤外包装。 This high density polyethylene is an ethylene-hexene copolymer tailored for blown film applications that require: High stiffness Excellent film drawdown Exceptional processability Blending with LLDPE and LDPE Typical blown film applications include: Notion and millinery bags Multi-wall liners Coextrusions Overwraps |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.956 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.75 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
0.25 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
841 | MPa | ASTM D882 |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
1070 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
氧气传输速率 Oxygen transfer rate |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g/m²/24 hr | ASTM F1249 | |
落锤冲击 Drop hammer impact |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
kN/m | ASTM D1709 | |
撕裂强度 tear strength 2 |
ASTM D1922 | ||
MD,25.4 µm MD,25.4 µm |
kN/m | ASTM D1922 | |
TD,25.4 µm TD,25.4 µm |
kN/m | ASTM D1922 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部 ![]()
经济日报:仅靠罚款解决不了快递上门难
2022-01-18 搜料网资讯: 近日,国家邮政局就《快递市场管理办法(修订草案)》公开征求意见。其中,对快递行业末端投递服务规范进行了明确:未经用户同意,不得代为确认收到快件,不得擅 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |